BT25钛合金棒材的组织和性能研究 被引量:2

Study on Microstructure and Mechanical Property of BT25 Titanium Alloy Bar
下载PDF
导出
摘要 依据BT25钛合金材料的特性,编制相应的试生产工艺,制备出Φ200mm的较大棒材和Φ20mm的较小棒材。测得的两类棒材的性能都满足了标准要求。在实验条件相同的情况下,轧制的小棒材并没有因为变行量增大而使性能得到极大提高,两者的性能差别不大,而且,两种规格棒材的显微组织都为等轴组织。 A trial process routine was determined to prepare BT25 bars with diameters of 200 mm and 20 mm according to the characteristics of the alloys. The traditional forging and combination of water quenching and air cooling were applied. In addition, rolling process was carried out at 60 centigrade below a/β phase transformation temperature, then water-quenched. The mechanical properties of final products reached the requirement of corresponding standards. Under the same experimental conditions, the properties of the rolling bars were not superior to those of the forging bars, and their microstructures are both equiaxed.
出处 《钛工业进展》 CAS 2009年第2期28-30,共3页 Titanium Industry Progress
关键词 钛合金 棒材 力学性能 显微组织 titanium bar mechanical properties microstructure
  • 相关文献

参考文献1

二级参考文献4

共引文献5

同被引文献24

  • 1赵永庆,奚正平,曲恒磊.我国航空用钛合金材料研究现状[J].航空材料学报,2003,23(z1):215-219. 被引量:125
  • 2袁少冲,毛小南,张鹏省,于兰兰,洪权.热强钛合金BT25组织与性能[J].钛工业进展,2006,23(3):19-22. 被引量:9
  • 3付艳艳,宋月清,惠松骁,米绪军.航空用钛合金的研究与应用进展[J].稀有金属,2006,30(6):850-856. 被引量:181
  • 4The Editorial Commillee of《中国航空材料手册编委员》《航空材料手册》[ M ]. BeiJing: China StandardPress, 2002.
  • 5赴英考察“钛合金”技术报告[ R]. Third Machanical Industry Ministry, 1978.
  • 6闵新华,朱益潘.刘金生.TAl5铁合金大规格悻材的锻造[J].稀有金属材料与工程2008.37(Suppl.3):250-252.
  • 7史正敏.6242S高温钛合金板材的组织特点[J].中国钛业,2007,12(3):32-35.
  • 8王晓英,周建华,庞克昌、TCl7钛合金盘轴等温精密锻件[J].稀有金属材料与工程,2008,37(Suppl.3):227-229.
  • 9魏寿庸王鼎春,雷家峰.BT22及其改进型钛合金[J].中国钛业,2007(3):21-27.
  • 10赵永庆,曲恒磊,陈军.损伤容限钛合金研究[J].稀有金属材料与工程),2008,37(Supp.3):26-29.

引证文献2

二级引证文献18

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部