SA-335P22高压锅炉管缺陷分析及改进措施 被引量:4

Analysis of SA-335P22 High Pressure Boiler Tube Defect and Its Improving Measure
原文传递
导出
摘要 SA-335P22高压锅炉管穿孔后管体表面出现大量裂纹,其形貌特殊且分布无规律。通过对裂纹进行金相和扫描电镜分析,以及对铸坯酸洗和低倍酸浸分析,确定该穿孔裂纹是由铸坯内部裂纹引起。采取降低中间包的过热度,适当降低拉坯速度,减小铸坯的二次冷却强度等措施,对减少这种缺陷的出现有明显的效果。 A lot of external cracks were found after piercing of SA-335P22 high pressure boiler tube bloom, and their pattern are special and distribute randomly. Cracks were analyzed by using optical and scan electronic microscope and acid leaching test of bloom and acid leaching sample test. The result showed that the defect is caused by bloom' s internal fine cracks. Measures of lower liquid superheat, decreasing the casting speed of bloom and reduction billet's secondary cooling strength are obviously effective to reduce such kinds of defects.
作者 刘合萍 田研
出处 《钢铁》 CAS CSCD 北大核心 2009年第6期97-100,共4页 Iron and Steel
关键词 高压锅炉管 内部裂纹 连铸圆管坯 high pressure boiler tube inner crack continuous casting round bloom
  • 相关文献

参考文献3

二级参考文献7

  • 1蔡开科 程士富.连续铸钢原理与工艺[M].北京:冶金工业出版社,2002.344.
  • 2.连续铸钢手册[M].北京:冶金工业出版社,1991..
  • 3李为--,钢中的非金属夹杂物,1988年
  • 4王北朝,热轧钢管的质量,1987年
  • 5陈家祥,炼钢常用图表数据手册,1984年
  • 6曲英,物理化学和炼钢,1984年
  • 7田党 李莹.连铸圆坯纵向裂纹缺陷研究[J].天津钢管,1996,.

共引文献31

同被引文献27

引证文献4

二级引证文献17

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部