摘要
对穿孔无缝钢管热穿孔顶头的失效机制和使用状况进行了分析研究,认为穿孔顶头的失效形式主要表现为顶头塌鼻、粘钢、开裂,提出了利用稀土铝合金化提高顶头使用寿命的措施,并对该措施的可行性进行了论证。
The failure mechanism and service status quo of hot piercer point in seamless steel tube were analyzed and its failure was mainly caused by piercer point col- lapsing nose ,sticking steel and cracking. One way to enhance the service life of piercer point by means of Re-Al alloying was offered and its feasibility was proved in this pa- per.
出处
《钢铁研究》
CAS
1998年第4期35-38,共4页
Research on Iron and Steel
基金
冶金部资助
关键词
热穿孔顶头
稀土铝合金化
高温性能
失效分析
hot piercer point Re - Al alloying failure mechanism high temper- ature property