燃煤锅炉锅筒开裂失效分析 被引量:2

Failure Analysis of Coal-fired Boiler Drum Dehiscence
下载PDF
导出
摘要 利用JXA-8800R电子探针对燃煤锅炉锅筒的缺陷进行分析。结果表明:锅筒钢板组织不合格,同时锅垢还使锅筒钢板表面产生较大的应力,致使钢板产生显微裂纹并扩展,以至最后开裂。最后提出了相应的改进措施。 JXA-8800R electron probe was used to analyze the defects from microscopic part. The results show that, the microstructure of the boiler steel is unqualified and great stress appears on the surface of drum caused by boiler scale, so micro-crack appears and grows on the surface of boiler steel which leads to dehiscence. At last, the preventive measures were put forward.
出处 《热加工工艺》 CSCD 北大核心 2009年第18期148-150,共3页 Hot Working Technology
关键词 锅炉材料 开裂 金相 失效分析 boiler material dehiscence metallic phase failure analysis
  • 相关文献

参考文献3

二级参考文献3

  • 1李东辉,邱以清,刘相华,王国栋.连铸凝固传热过程的数值模拟[J].铸造技术,2004,25(7):529-531. 被引量:19
  • 2BealyM,Henien H. Finite difference heat-Transfer modeling for continuous casting [J]. Metallurgical Transactions, 1993, (6): 85-93.
  • 3宋维锡.金属学[M].北京:冶金工业出版社,1980..

共引文献8

同被引文献15

引证文献2

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部