渗氮方式及氨气对取向硅钢氮含量的影响 被引量:9

Influence of nitriding modes and ammonia on nitrogen content of oriented silicon steel
原文传递
导出
摘要 研究渗氮气氛中不同氨气比例及喷射与非喷射渗氮方式对取向硅钢氮含量的影响,对渗氮前后样品表层氧化膜变化进行比较。结果表明,氧化膜厚度为0.1μm的硅钢片在渗氮温度为750℃,氨气量为1%-5%条件下渗氮时短时间内渗氮效果不明显,氨气量为10%-40%的气氛渗氮效果明显。随着氨气比例的增加,硅钢片中的氮含量增加,当氨气量为30%时,喷氮方式渗氮后的硅钢片渗氮量是非喷氮方式的2.5倍。此外,渗氮气氛中的氢气可以还原氧化膜厚度的20%。 The effects of ammonia proportion and the nitriding modes of spraying as well as non-spraying on nitrogen content in oriented silicon steel were studied. The change of oxidation film before and after nitriding is analyzed. The results show that the nitriding which is proceeded in the steel with the oxide film of 0. 11μm at 750 ℃, 1% -5% (volume percentage) NH3 has no prominent nitriding effect in a short time. However,the nitriding effect is prominent when volume percentage of NH3 is 10% -40%. With increasing the volume percentage of NH3 ,the nitrogen content increases. When the volume percentage of NH3 is 30% ,nitrogen content by spraying nitriding mode is 2. 5 times as much as that by non-spraying. Hydrogen in the nitriding atmosphere can deoxide the thickness of the oxidation film by 20%.
出处 《金属热处理》 CAS CSCD 北大核心 2009年第10期69-71,共3页 Heat Treatment of Metals
基金 湖北省自然科学基金(2006ABA292)
关键词 取向硅钢 氨气 渗氮 氧化膜 oriented silicon steel ammonia nitriding oxidation film
  • 相关文献

参考文献8

二级参考文献38

  • 1席守谋,郝立博.钢箔称重法测量气氛氮势初探[J].材料工程,1996,24(1):36-37. 被引量:6
  • 2王小燕,刘学华,姚静.薄板坯连铸连轧生产电工钢现状及其优势[J].钢铁研究,2006,34(3):58-62. 被引量:9
  • 3胡光立 谢希文.钢的热处理[M].西安:西北工业大学出版社,1992.25.
  • 4庄永迪.物理化学基础[M].西安:西北工业大学出版社,1984.36.
  • 5潘健生.氮势控制原理与可渗渗氮的生产经验[J].金属热处理,1982,57(5):13-13.
  • 6李崇谋.氮势的定义[J].金属热处理,1980,36(8):35-35.
  • 7Klaus Gunther. Recent technology development in the production of grain oriented electrical steel [J]. Steel Research International, 2005, 76(6) :413-421.
  • 8牛神羲行.冷轧前析出处理对取向电磁钢二次再结晶的影响.电工钢,2005,61(3):55-55.
  • 9Matsuo Munetsugu. Origin and development of through-the-thickness variations of texture in the processing of grain-oriented silicon steel [ J ]. Metallurgical and Materials, 1986,17 A ( 8 ) : 1313-1322.
  • 10Shimizu Y. Formation of the Goss orientation near the surface of 3 Pet silicon steel during hot wiling[ J]. Metallurgical and Materials, 1986, 17A(8) : 1323-1334.

共引文献79

同被引文献52

  • 1秦开明,刘冬梅,于翔,顾艳红.温度对离子渗氮渗层厚度及表面硬度的影响[J].石油地质与工程,2004,19(5):60-61. 被引量:4
  • 2Yubui SHA,Fang ZHANG,Song LI,Xaoyu GAO,Jiazhen XU,Liang ZUO School of Materials and Metallurgy,Northeastern University,Shenyang 110004,China.Effects of Primary Annealing Condition on Recrystallization Texture in a Grain Oriented Silicon Steel[J].Journal of Materials Science & Technology,2004,20(3):253-256. 被引量:9
  • 3董如何,肖必华,方永水.正交试验设计的理论分析方法及应用[J].安徽建筑工业学院学报(自然科学版),2004,12(6):103-106. 被引量:238
  • 4周潘兵,周浪.氧化层对渗氮动力学的影响[J].材料热处理学报,2005,26(4):102-105. 被引量:25
  • 5Klaus Gunther. Recent technology development in the production of grain oriented electrical steel [J].Steel Research International, 2005, 76:413-421.
  • 6Lee C S. Method for manufacturing high magnetic flux density grain oriented electrical steel based on low temperature slab heating method: US,6151128[P]. 2002-09-17.
  • 7Munetsugu Matsuo. Texture control in the production of grain oriented silicon steels[J]. ISIJ International, 1989,29(10) :809-812.
  • 8何忠冶.电工钢[M].北京:冶金工业出版社.1997:587.
  • 9Hotaka Homma, Bevis Hutchinson. Orientation dependence of secondary recrystallisation in siliconiron [J]. Acta Materialia, 2003, 51:3 795-3 805.
  • 10Tomoji Kumano. Grain boundary characteristics in grain oriented silicon steel [J]. ISIJ International, 2004, 44(11):1 888-1 893.

引证文献9

二级引证文献43

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部