超声处理温度区间对镁合金凝固组织的影响 被引量:2

Effect of the Temperature Range for Ultrasonic Treatment on Solidification Structure of Magnesium Alloy
下载PDF
导出
摘要 研究了超声处理温度区间对AZ91D和AZ31B镁合金凝固组织的影响,探讨了功率超声细化镁合金凝固组织的机理。试验结果表明,镁熔体经超声处理后,凝固组织均有显著细化,其中超声连续处理对镁合金的细化效果最好。 The effect of temperature range for ultrasonic treatment on solidification structure of AZ91D and AL6115 magnesium alloy was investigated and the mechanism of refining solidification structure of magnesium alloy by power ultrasonic treatment was discussed. The experimental results showed that the solidification structure of magnesium melt were all refined remarkably after ultrasonic treatment and the finest refining effect on magnesium alloy was obtained by continuous ultrasonic treatment.
出处 《矿冶工程》 CAS CSCD 北大核心 2009年第5期94-97,共4页 Mining and Metallurgical Engineering
基金 江西省自然科学基金(0650090) 江西省教育厅科技计划项目(200614) 江西省科技攻关项目(S0006)
关键词 镁合金 凝固 超声处理 温度区间 细化机制 magnesium alloy solidification ultrasonic treatment temperature range refinement mechanism
  • 相关文献

参考文献7

二级参考文献11

共引文献210

同被引文献28

引证文献2

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部