摘要
采用铸锭冶金工艺,制备不同钪含量的Al-Cu-Mg-Ag合金。通过金相显微镜、扫描电镜、透射电镜、晶间腐蚀及剥落腐蚀等实验方法,研究钪对Al-5.3Cu-0.8Mg-0.6Ag合金的组织和腐蚀性能影响。结果表明:添加0.3%～0.5%Sc可明显细化铸态合金的晶粒,平均晶粒尺寸从300μm降低到60μm,而添加0.1%～0.3%Sc有助于提高挤压态合金抗腐蚀性能。但当添加0.5%Sc时,合金中形成粗大的Al3(Sc,Zr)稀土化合物相,导致合金的抗蚀性能降低。
The Al-Cu-Mg-Ag alloys with different scandium contents were prepared by ingot metallurgy technology.The effect of scandium addition on microstructure and corrosion properties of Al-5.3Cu-0.8Mg-0.6Ag-0.2Zr alloy was investigated using optical microscope,scanning electron microscope（SEM）,transmission electron microscope（TEM）,intergranular corrosion and exfoliation corrosion.The result shows that 0.3% 0.5%Sc addition refines the grains of the casting alloys and the average grain size decreases from 300μm to 60μm.Increasing Sc content from 0.1%to 0.3% increases corrosion-resistance properties of the extruded alloys.However,the coarsening Al3（Sc,Zr）compounds in the extruded alloys with 0.5%Sc decrease corrosion-resistant properties seriously.
出处
《中南大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2009年第5期1252-1258,共7页
Journal of Central South University:Science and Technology
基金
中国博士后科学基金资助项目(20070410986)
中南大学博士后科学基金资助项目(2007年)
中国博士后特别资助科学基金资助项目(200801348)