等径角挤压制备CuCrZr合金的抗软化性能 被引量:2

Softening resistance of CuCrZr alloy fabricated by equal channel angular pressing
原文传递
导出
摘要 研究了CuCrZr合金等径角挤压(ECAP)后的微观组织演变及软化温度。结果表明,固溶态CuCrZr合金经路线BC(每挤一道次后试样沿同一方向旋转90°)等径角挤压10道次后组织细化至亚微米级,超细晶晶粒较为等轴、均匀。等径角挤压10道次后合金的软化温度约为530℃,但550℃时,合金的硬度仍高达161HV,这说明ECAP后合金的抗软化能力并没有降低。因为ECAP促进了时效时析出相的析出,使得析出相更为弥散、细小,从而提高了合金的力学性能。 Microstructure evolution and softening temperature of CuCrZr alloy after equal channel angular pressing(ECAP) were investigated.The results show that the grains of solid-solutioned CuCrZr alloy are refined to sub micrometer level after ECAP for 10 passes with route BC(the sample is rotated sequentially by 90°around its axis).The ultra-fine grains are more equiaxed and homogeneous.The softening temperature is about 530℃,however,vickers hardness even remains 161HV at 550℃ for the 10 passes ECAPed sample,which indicates that the softening resisitance of CuCrZr alloy does not decrease after ECAP.It is argued that the precipitation of dispersed and fine precipitates is accelerated by the ECAP and thus mechanical properties of the alloy are improved.
出处 《材料热处理学报》 EI CAS CSCD 北大核心 2009年第6期94-97,共4页 Transactions of Materials and Heat Treatment
基金 国家自然科学基金资助项目(50575097) 江苏大学科技创新团队项目(08JDK011)
关键词 等径角挤压 CUCRZR合金 软化温度 超细晶 equal channel angular pressing CuCrZr alloy softening temperature ultra-fine grains
  • 相关文献

参考文献10

二级参考文献73

共引文献115

同被引文献28

  • 1石凤健,王雷刚,王海龙,汪建敏.等径角挤压工艺对固溶状态CuCrZr合金性能的影响[J].金属热处理,2007,32(1):81-83. 被引量:4
  • 2Valiev R Z, lslamgaliev R K,Alexandrov I V. Bulk nanostructured materials from severe plastic deformation [ J]. Progress in Materials Science,2000,45(2) :103 - 189.
  • 3Valiev R Z, Langdon T G. Principles of equal-channel angular pressing as a processing tool for grain refinement [ J ]. Progress in Materials Science, 2006,51 (7) :881 -981.
  • 4Kai M, Horita Z, Langdon T G. Developing grain refinement and superplasticity in a magnesium alloy processed by high-pressure torsion [ J ]. Materials Science and Engineering A ,2008,488 ( 1 - 2 ) : 117 - 124.
  • 5Shaarbaf M, Toroghinejad M R. Nano-grained copper strip produced by accumulative roll bonding process [ J]. Materials Science and Engineering A, 2008,473 (1 -2) :28 -33.
  • 6Xing J,Yang X Y, Miura H,et al. Grain refinement in Magnesium alloy AZ31 during multidirectional forging under decreasing temperature conditions [ J ]. Materials Science Forum ,2005,488 -489:597 - 600.
  • 7Miura H, Nakao Y, Sakai T. Enhanced grain refinement by mechanical twinning in a bulk Cu-30mass% Zn during muhi-dlrectional forging [ J]. Materials Trartsaetions ,2007,48 (9) :2539 - 2541.
  • 8Azushima A, Kopp R, Korhonen A, et al. Severe plastic deformation (SPD) processes for metals [ J ]. CIRP Annals-Manufacturing Technology,2008, 57(2) :716 -735.
  • 9Gubicza J,Nam N H, Balogh L,et al, Microstructure of severely deformed metals determined by X-ray peak profile analysis[ J]. Journal of Alloys and Compounds, 2004,378 ( 1 - 2 ) : 248 - 252.
  • 10Xue Q,Beyerlein I J, Alexander D J, et al. Mechanisms for initial grain refinement in OFHC copper during equal channel angular pressing[ J ]. Acta Materialia ,2007,55 ( 2 ) :655 - 668.

引证文献2

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部