含钴PDMS/三甲基硅基甲基纤维素复合膜的富氧性能研究

Study on oxygen-enriching properties of Trimethylsilyl methylcellulose/silicone rubber Cobalt-Containing composite Membranes
下载PDF
导出
摘要 以乙烯基质量分数为5%的硅橡胶为基质材料,加入一定量的三甲基硅基甲基纤维素,以含氢硅油为交联剂、氯铂酸为催化剂,通过硅氢加成反应,将羧酸钴结构键合到膜内的交联网络中,室温硫化成膜。膜的富氧性能研究表明,在硅橡胶交联网络中,混入三甲基硅基甲基纤维素,不仅提高了分离系数,也改善了成膜性和膜强度。由于三甲基硅基甲基纤维素(TMS-MC)的混入,20℃时氧氮分离系数(α)升高到3.7,透氧系数(P)稍有降低为437Barrer。 A silicone rubber composite membrane with heavily crosslinked structure was prepared from silicone rubber containing 5% vinyl groups (molar fraction) and trimethylsilyl methylcellulose with silicone oil containing hydrogen as crosslinking agent,and chloroplatinic acid as catalyst by solvent casting and vulcanizing at room temperature, its oxygen enriching properties were investigated. The results show that addition of trimethylsilyl methylcellulose into crosslinking network of silicone rubber not only increases separation coefficient, but also improves film forming ability and film strength, its oxygen/nitrogen separation coefficient (αO2/N2 ) increases to 3.7 at 20 ℃ and oxygen permeability coefficient (PO2) slightly decreases to 437 Barrer because of addition of trimethylsilyl methylcellulose.
作者 吴新华 石慧
出处 《辽宁化工》 CAS 2009年第12期847-849,874,共4页 Liaoning Chemical Industry
关键词 硅橡胶 甲基纤维素 富氧性能 Silicone Rubber Trimethylsilyl Methylcellulose Oxygen - Enriching
  • 相关文献

参考文献11

二级参考文献24

  • 1陈学信,梁少文,林尚安.三元乙丙胶磺酸盐离聚物富氧膜的研究[J].功能高分子学报,1993,6(2):163-168. 被引量:1
  • 2张子勇,林尚安.有机金属络合物用于高分子富氧膜的研究进展[J].高分子通报,1994(4):200-207. 被引量:4
  • 3[1]Way J. D., Noble R. D.. Membrane Handbook[M], New York: Van Nostrand Reinhold, 1993: 833-866
  • 4[2]Nishide H., Tsuchida E.. Macromolecules-Metal Complexes[M], Berlin: Springer-Verlag, 1996: 175-190
  • 5[3]Nishide H., Ohyanagi M., Okada O. et al.. Macromolecules[J], 1987, 20: 417-422
  • 6[4]Nishide H., Tsukahara Y., Tsuchida E.. J. Phys. Chem.[J], 1998, B102: 8 766-8 770
  • 7[5]Collman J. P., Gagne R. R., Reed C. A. et al.. J. Am. Chem. Soc.[J], 1975, 97: 1 427-1 439
  • 8[7]Nishide H., Kawakami H., Suzuki T. et al.. Macromolecules[J], 1991, 24: 6 306-6 309
  • 9[8]Lynn M. M., Worm A. T.. Encyclopedia of Polymer Science and Technology, Vol.7[M], New York: John Willy, 1987: 256-269
  • 10[9]Kita H., Shigekuni M., Kawafune I. et al.. Polymer Bulletin[J], 1989, 21: 371-376

共引文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部