水性双组分聚氨酯涂料的活化期研究 被引量:9

Investigation into Pot Life of Waterborne Two-Component Polyurethane Coatings
下载PDF
导出
摘要 分别采用水性羟基聚丙烯酸酯分散体(PAD)和羟基聚丙烯酸酯乳液(PAE)与亲水改性多异氰酸酯固化剂配制水性双组分聚氨酯涂料(2K-WPU),通过黏度、硬度、光泽度和耐化学介质性能等测试,研究了2K-WPU在不同放置时间内的物理化学行为.结果发现:随放置时间的增加,PAD型2K-WPU的黏度降低,涂膜的起泡程度逐渐增加,涂膜硬度先降低后增加,3h后耐化学介质性能下降;PAE型2K-WPU的黏度变化无规律,涂膜硬度逐渐降低,4h后耐化学介质性能下降,气泡相对较少;PAD型和PAE型2K-WPU的粒径和光泽均无明显变化;PAE型2K-WPU的活化期一般在4h以内,而PAD型的更短,但涂膜的综合性能更优.因此施工前不能根据2K-WPU的黏度变化来判断其活化期,而须根据涂膜耐化学介质性能和外观变化来判断。 Waterborne two-component polyurethane (2K-WPU) coatings were prepared from hydrophilically-modifled polyisocyanate reacting respectively with an aqueous hydroxy-polyacrylate emulsion (PAE) and its dispersion (PAD). Then, the viscosity, hardness, gloss and chemical resistance of the films were measured to investigate the physicochemical behaviours of 2K-WPU during the storage. The results indicate that ( 1 ) with the increase of storage time, the viscosity of PAD-based 2K-WPU slowly decreases, along with an increase in bubbles and micro-foams in the film, the film hardness first decreases and then increases, and the chemical resistance decreases after a storage for 3h; (2) as for PAE-based 2K-WPU, the viscosity disorderly changes, the film hardness gradually decreases, the chemical resistance decreases after a storage for 4 h, and the bubbles in the film even disappear; (3) neither the particle diameter nor the gloss of PAE- and PAD-based 2K-WPU shows obvious change during the storage; and (4) PAD-based 2K-WPU is of better film performance but slightly shorter pot life than the PAE-based one (about 4 h). It is thus concluded that it is not the viscosity but the chemical resistance and appearance of the film that determine the pot life of 2K-WPU before the application.
出处 《华南理工大学学报(自然科学版)》 EI CAS CSCD 北大核心 2009年第12期85-89,94,共6页 Journal of South China University of Technology(Natural Science Edition)
基金 粤港关键领域重点突破项目招标课题(B10-B2050260)
关键词 双组分聚氨酯涂料 活化期 水性羟基聚丙烯酸酯 亲水改性多异氰酸酯 固化剂 two-component polyurethane coating pot life waterborne hydroxy-polyacrylate hydrophilicallymodified polyisocyanate curing agent
  • 相关文献

参考文献10

  • 1Ingo A, Sascha T, Peter K, et al. Characterization of coating systems by scanning acoustic microscopy:debonding, blistering and surface topology [ J ]. Progress in Orgariic Coatings ,2009,64 (2/3) : 112-119.
  • 2Wicks Z W, Wicks D A, Rosthauser J W. Two package waterborne urethane systems [ J ]. Progress in Organic Coatings ,2002,44 ( 2 ) : 161-183.
  • 3Melchiors M, Sonntag M, Kobusch C, et al. Recent developments in aqueous two-component polyurethane coatings [ J ]. Progress in Organic Coatings, 2000,40 ( 1/2/3/4 ) : 99-109.
  • 4Tama T, Ito S. Preparation and reactions of hydrophilic isocyanate micelles dispersed in water [ J ]. Colloid & Polymer Science,2005,283 ( 7 ) : 731-737.
  • 5瞿金清,李佩妍,陈焕钦.甲基丙烯酸甲酯与水性聚氨酯的共聚反应[J].华南理工大学学报(自然科学版),2004,32(8):54-57. 被引量:24
  • 6Denise E F, David A L, Richard J Q. Effect of particle size distribution on the performance of two-component water- reducible acrylic polyurethane coatings using tertiary polyisocyanate erosslinkers [ J ]. Journal of Coating Technology,2000,72 (902) :63-69.
  • 7Geurink P J, Scherer T, Buter R, et al. A complete new design for waterborne 2-pack PUR coatings with robust application properties [ J ]. Progress in Organic Coatings, 2006,55(2) : 119-127.
  • 8瞿金清,罗春晖,陈焕钦.水性聚氨酯-丙烯酸酯的交联改性及涂膜性能[J].华南理工大学学报(自然科学版),2009,37(6):53-57. 被引量:18
  • 9瞿金清,涂伟萍,陈焕钦.双组分水性聚氨酯涂料的合成与表征[J].高校化学工程学报,2002,16(2):212-216. 被引量:68
  • 10周新华,涂伟萍,胡剑青.Preparation and Characterization of Two-component Waterborne Polyurethane Comprised of Water-soluble Acrylic Resin and HDI Biuret[J].Chinese Journal of Chemical Engineering,2006,14(1):99-104. 被引量:50

二级参考文献31

  • 1瞿金清,李佩妍,陈焕钦.甲基丙烯酸甲酯与水性聚氨酯的共聚反应[J].华南理工大学学报(自然科学版),2004,32(8):54-57. 被引量:24
  • 2Yang S, Petschke G. Air curable water-borne urethaneacrylic hybrids : US,6239209 [ P]. 2001-12-08.
  • 3Wang Shih-Chieh, Chen Po-Cheng, Yeh Jen-Taut, et al. A new curing agent for self-curable system of aqueous-based PU dispersion [ J ]. Reactive and Functional Polymers, 2007,67 (4) : 299-311.
  • 4Coogan A G. Post-crosslinking of waterborne urethans [ J ]. Progess in Organic Coatings,1997,32(1/2/3/4) :51-63.
  • 5Lai J Z, Ling H J, Chen G N, et al. Polymer hybrids from self-emulsified PU anionomer and water-reducible acrylate copolymer via a postcuring reaction [ J ]. Journal of Applied Polymer Science, 2003,90 ( 4 ) : 3 578-3 587.
  • 6Lai J Z, Ling H J, Chen G N, et al. New self-curable, aqueous-based polyurethane system by an isophorone diisocyanate/uretedione aziridinyl derivative process [ J ]. Journal of Applied Polymer Science, 2004,94 ( 2 ) : 845- 859.
  • 7[3]Hegedus C R, Kloiber K A. Aqueous acrylic-polyurethane hybrid dispersions and their use in industrial coatings [J]. Journal of Coating Technology, 1996, 68(860) :39 -48.
  • 8[4]Irle C, Blum H, Kremer W. Self crosslinkable polyurethane-polyacrylate hybrid dispersions[P]. US: 6063861,2000 - 6 - 10.
  • 9[5]Yang S, Petschke G. Air curable water-borne urethane-acrylic hybrids [P]. US :6239209,2001 - 12 - 8.
  • 10[6]Hirose M, Kadowaki F, Zhou J H. The structure and properties of core-shell type acrylic-polyurethane hybrid aqueous emulsions [J]. Progress in Organic Coatings,1997,31:157 - 169.

共引文献151

同被引文献59

引证文献9

二级引证文献22

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部