PA6/PTT共混物的吸水性和力学性能 被引量:12

Water Absorptivity and Mechanical Properties of PA6/PTT Blends
下载PDF
导出
摘要 由螺杆挤出机制备了尼龙6(PA6)和聚对苯二甲酸丙二醇酯(PTT)的共混物PA6/PTT。通过浸水实验,结合扫描电镜观察和热分析,研究了不同组分PA6/PTT共混物的吸水性能,并进行了相关力学性能测试。结果表明,PA6/PTT共混物吸水率随PTT含量增加而减小,即PTT的加入有效抑制了PA6的吸水率;在相同吸水条件下,PA6/PTT共混物的一般力学性能明显优于PA6,当PTT含量为20%时,共混物吸水后的拉伸、弯曲强度分别较PA6提高了20.98%和71.73%。 PA6/PTT blends were prepared by twin screw extruders after mixing poly(trimethylene terephthalate) (PTT) with polyamide 6 (PA6). The water absorptivity of the PA6/PTT blends was investigated by water immersion tests in combination with scanning electron microope (SEM) and differential scanning calorimetry (DSC). General mechanical properties tests were also conducted in this paper. The results show that the amount of absorbed water in the blends decreases with the increase of PTT content, which indicates that the PTT phase can effectively restrain the PA6 phase from absorbing water. Mechanical tests also show that after absorbing water under the same conditions the general mechanical properties of PA6/PTT blends are obviously better than those of pure PA6. When the PTT content is 20%, the tensile and bending yield strength of PA6/PTT after absorbing water is improved by 20.89 % and 71.73 % respectively as compared to those of pure PA6.
出处 《高分子材料科学与工程》 EI CAS CSCD 北大核心 2010年第2期73-76,共4页 Polymer Materials Science & Engineering
基金 湖南省教育厅资助项目(07A071 08C893) 国家自然科学基金资助项目(10672138)
关键词 尼龙6 聚对苯二甲酸丙二醇酯 共混物 吸水性 力学性能 PA6 PTT blends water absorptivity mechanical properties
  • 相关文献

参考文献9

二级参考文献57

共引文献67

同被引文献221

引证文献12

二级引证文献108

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部