P110油管钢稀土渗铬工艺优化 被引量:1

Process Optimization of RE Modified Chromizing for P110 Oil Tube Steel
下载PDF
导出
摘要 利用正交试验方法对P110油管钢(P110钢)稀土渗铬工艺参数进行优化。结果表明:采用试验中的每组工艺参数,均可在P110钢表面形成连续、均匀、致密的渗铬层;以渗层的成分厚度(wCr≥12%)作为评价指标,得到的优化工艺参数为:温度1000℃,保温时间8 h,催化剂含量3wt%,稀土添加量7wt%。 An orthogonal designing method was used to optimize processing parameters of rare earth (RE) modified chromizing on P110 oil casing tube steel (P110 steel). The results show that the chromizing coating is available based on each processing parameter, the coating is uniform, continuous and compact. Taking the compositional thickness (wCr≥12%) as an evaluating indicator, the optimal process parameters are obtained as follows: chromizing temperature 1000 ℃, holding time 8 h, and activator composition 3wt%, RE addition ratio 7wt%.
出处 《热加工工艺》 CSCD 北大核心 2010年第2期137-138,141,共3页 Hot Working Technology
基金 陕西省科学技术研究发展计划资助项目(2008K01-31)
关键词 油管钢 稀土 渗铬 工艺优化 oil tube steel rare earth(RE) chromizing process optimization
  • 相关文献

参考文献10

二级参考文献70

共引文献195

同被引文献5

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部