为从醋酸正丁酯稀水溶液中回收微量酯,采用涂布法制备了聚醚共聚乙酰胺/聚偏氟乙烯(PEBA/PVDF)复合膜.考察了复合膜在醋酸正丁酯稀水溶液中的溶胀性能,探讨了浸泡时间、浸泡液温度及浸泡液浓度等因素对溶胀度的影响.通过拉力试验,测试了复合膜的力学性能.通过渗透汽化实验,从醋酸正丁酯稀水溶液中分离出醋酸正丁酯,研究了料液浓度、料液温度等因素对复合膜分离性能的影响.结果显示,复合膜在醋酸正丁酯稀水溶液中具有良好的溶胀性能及渗透汽化性能;40℃下分离质量分数为0.6%的醋酸正丁酯水溶液,渗透通量达到280.43 g/(m2.h),分离因子为308.65.
The aim of this work is to recycle trace N block amide/poly（vinylidene fluoride） （PEBA/PVDF） - butyl acetate from dilute aqueous solution. Polyether composite membrane was prepared by cast. The swelling behavior of membrane in N - butyl acetate dilute aqueous solution was explored. The effect of dipping time, temperature as well as concentration on the swelling degrees was also measured. Mechanical property of the membrane was investigated by stretching test. N - butyl acetate was separated from its aqueous solution by per- vaporation experiments. The influence of feed concentration and temperature on separation performance of the membrane was tested. The results of swelling and pervaporation experiments show the membrane has very nice swelling and pervaporation behavior in N - butyl acetate aqueous solution. The flux and separation factor are 280.43 g/（m2. h） and 308.65, respectively, at 40 ℃ as well as 0.6 % （mass fraction） feed concentration.
出处
《膜科学与技术》
CAS
CSCD
北大核心
2010年第1期60-64,共5页
Membrane Science and Technology
基金
广西留学回国基金(桂科回0575002)
"广西区教育厅研究生创新基地建设"项目