高温钛合金Ti-60粉末的制备和表征 被引量:4

Preparation and Characterization of High Temperature Titanium Alloy Ti-60 Powders
原文传递
导出
摘要 采用感应熔炼气体雾化法制备了掺杂稀土Nd的高温钛合金Ti-60粉末。结果表明,在制备过程中合金元素几乎没有烧损,增氧量小于100×10^(-6);粉末的平均粒度(d_(50))约为100μm,满足正态分布,雾化气体的压力增大则粉末的粒度减小;粉末的形貌大多呈球形,只有少量的形状不规则;部分粉末是空心的,其比例随着粉末粒度的增加而增大;粉末表面有明显的凝固特征,具有清晰的二次枝晶;随着Nd含量的增加,粉末表面富Nd稀土相的析出增加;粉末由针状α′马氏体组织构成,当真空退火温度超过700℃时马氏体开始微量分解,当温度升高到850℃时马氏体大量分解。 The high temperature titanium alloy Ti-60 powder was prepared by Electrode Induction Melting Gas Atomization(EIGA) method.The variation in chemistry between nominal composition and powder was minimal and the increment of oxygen during gas atomization was less than 100×10^-6,which insured the alloy composition and purity of the powder.The powder size distribution followed Gaussian distribution and the medium diameter(d50) was about 100μm,which was decreased with the increasing of argon gas pressure during atomization process.The powder was nearly spherical and some powder particles were irregular.Some powders were hollow and the percentage of the hollow powder increased with the increase of powder diameter.The powder surface showed an obvious characteristic of solidification with distinct secondary dendrite and the rich-neodymium phase became apparent with the increase of neodymium content.The powder microstructure was composed ofα' martensite phase formed upon the high rate solidification process,which decomposed at 700℃micro-contently and at 850℃heavily.
出处 《材料研究学报》 EI CAS CSCD 北大核心 2010年第1期10-16,共7页 Chinese Journal of Materials Research
基金 国家高技术研究发展计划2007AA03A224资助项目~~
关键词 金属材料 高温钛合金 气体雾化 Ti-60粉末 粒度分布 表观形貌 空心粉末 α′马氏体分解 metallic materials high temperature titanium alloy gas atomization Ti-60 powder power size distribution hollow powder surface graph α' martensite decomposition
  • 相关文献

参考文献10

  • 1F.H.Froes, S.J.Mashl, V.S.Moxson, V.A.Duz, The technologies of titanium powder metallurgy, JOM, 56(11), 46(2004).
  • 2V.S.Moxson, O.N.Senkov, F.H.Froes, Innovations in titanium powder processing, JOM, 52(5), 24(2000).
  • 3F.G.Arcella, F.H.Froes, Producing titanium aerospace components from powder using laser forming, JOM, 52(5), 28(2000).
  • 4M.Hagiwara, S.Emura, Blended elemental P/M synthesis and property evaluation of Ti-1100 alloy, Mater. Sci. Eng., A352(8), 85(2000).
  • 5C.Suryanarayana, F.H.Froes, R.G.Rowe, Rapid solidification processing of titanium-alloys, Int. Mater. Rev., 36(3), 85(1991).
  • 6G.Wegmann, R.Gerling, F.P.Schimansky, Temperature induced porosity in hot isostatically pressed gamma titanium aluminide alloy powders, Acta Mater., 51(3), 741(2003).
  • 7宗斌,魏建忠,王国红.金属粉末金相样品的制备方法[J].理化检验(物理分册),2005,41(4):210-211. 被引量:3
  • 8李素萍,毛协民,梁红玉,胡志恒.快速凝固雾化工艺对铝合金粉末形貌和粒度分布的影响[J].铸造技术,2005,26(4):264-267. 被引量:6
  • 9韩凤麟,马福康,曹勇家.中国材料工程大典-粉末冶金材料工程,第一版,(北京,化学工业出版社,2006)p.78.
  • 10T.E.MILES, J.F RHODES, Unique powder processing for ultimate shape and properties, in: Rapid Solidification Processing: Principles and Technologies; Proceedings of the international Conference, edited by Rober, Mehrabian, B.H.Kear, M.Cohen (Baton Rouge, Claitor's Pub, 1978) p.347.

二级参考文献21

  • 1刘峥,马如璋,赵钟涛.超细铁粉和氧化铁颗粒的研究[J].理化检验(物理分册),1994,30(3):17-20. 被引量:2
  • 2许炳炎,孙旭茂.体视显微镜摄影装置的改制[J].理化检验(物理分册),1994,30(5):58-58. 被引量:1
  • 3徐瑞,崔玉友,李东,胡壮麒,徐达鸣,李庆春.气体雾化Ti_3Al基合金的颗粒特征与结晶形貌[J].材料研究学报,1995,9(3):228-232. 被引量:5
  • 4陈兆定.影响金属粉末显微硬度测量的因素[J].物理测试,1996,14(2):34-35. 被引量:2
  • 5秦国有.定量金相[M].成都:四川科学技术出版社,1987.82.
  • 6刘国权.体视学[M].北京:冶金工业出版社,1989..
  • 7雷平.气体雾化Ti3Al基合金的颗粒特征与结晶形貌[J].理化检验:物理分册,2000,36(9):402-403.
  • 8C F Dixon, H M Skelly. Microstructure of rapidly solidi fied Al-Si alloy powders [J]. Int. J. Power Metal, 1965,1(4) :28-33.
  • 9H M Skelly, C F Dixon. Dynamical evolution of microstructure in finely atomiaed droplets of Al-Si alloys [J]. Int. J. Power Metal. 1971,7(3) :47-52.
  • 10I Yamauchi, I Ohnaka, S Kawamoto,etal. Production of Rapidly Solidified Al-Si Alloy Powder by the Rotating-Water-Atomization Process and Its Structure Trans[J].Japan. Inst. Met.. 1986,27:187-194.

共引文献7

同被引文献30

引证文献4

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部