超细25%NiCr-Cr_3C_2粉末制备及HVOF涂层性能研究 被引量:6

Research on Preparing of Ultrafine Cr_3C_2-25%NiCr Powders and Properties of HVOF Coating
下载PDF
导出
摘要 本文采用超细碳化铬粉末通过团聚烧结工艺制备球形25%NiCr-Cr3C2复合粉末,使用超音速火焰喷涂工艺制备耐高温磨损涂层,分析了超细25%NiCr-Cr3C2复合粉末的化学成分和表面形貌,通过涂层的结合强度和显微硬度与常规粉末的对比实验,研究超细Cr3C2颗粒对超音速火焰喷涂涂层的性能影响。 In this paper, a type of spherical Cr3C2-25% NiCr powders were prepared by agglomerated and sintered with ultrafine chromium carbide. Abrasion resistant coating was prepared using these powders by High Velocity Oxygen-Fuel spraying(HVOF). The chemical compounds and surface of Ultrafine CraC2-25%NiCr powders were analyzed. The influence of ultrafine Cr3C2-25%NiCr powders to coating is studied by compared experiments of bonding strength and hardness of the coating.
出处 《热喷涂技术》 2010年第1期20-23,共4页 Thermal Spray Technology
关键词 超细25%NiCr-Cr3C2复合粉末 超音速火焰喷涂 团聚烧结 Ultrafme Cr3C2-25%NiCr powders High velocity oxygen-fuel spray Agglomerate and sinter
  • 相关文献

参考文献2

二级参考文献1

  • 1Barbezat G,Tribology Transactions,1995年,4卷,138期,845页

共引文献25

同被引文献93

引证文献6

二级引证文献54

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部