核电站用板式换热器失效分析 被引量:5

Failure Analysis of Heat Exchanger Plate in Nuclear Power Plant
原文传递
导出
摘要 考察了核电站用钛板换热器裂纹和穿孔等失效现象,采用断口分析、表面宏观和微观形态分析、材料化学成分分析、金相组织分析等方法分析换热器失效原因。结果表明:钛板换热器成形加工的强烈变形区存在较严重的损伤缺陷,并且在工作中存在振动,是导致钛板换热器疲劳开裂失效的主要原因;海水侧微粒的冲蚀作用是换热钛板穿孔失效的主要原因。 The cracks,perforation failure phenomena of the titanium plate heat exchanger in the nuclear power plant were examined in this article.The fracture,macro-and micro-morphology,material composition and microstructure analysis methods were used to analysis the reason for the failures of heat exchanger.The results showed that it is the serious damage defects formed in the strong deformation zone of titanium heat exchanger during formation process and the vibration during service process,caused the failure of titanium heat exchanger by fatigue cracking.The perforation failure of plate was caused by the abrasion of the micro-particles from sea water.
机构地区 钢铁研究总院
出处 《物理测试》 CAS 2010年第2期55-59,共5页 Physics Examination and Testing
关键词 板式换热器 核电站 穿孔 疲劳 失效分析 heat exchanger plate nuclear power plant perforation fatigue failure analysis
  • 相关文献

参考文献2

  • 1RCC-P, Design and Construction Rules for PWR Nuclear Po wet Plants, Rules for System Design (2000)[S].
  • 2RCC-M, Design and Construction Rules for Mechanical Components of PWR Nuclear Islands (2000)[S].

同被引文献55

引证文献5

二级引证文献11

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部