功能型单层石墨烯的热剥离法制备及其超电容性能 被引量:22

Preparation of Functionalized Graphene Sheets by Thermal Exfoliation Approach and Their Electrochemical Supercapacitive Behavior
下载PDF
导出
摘要 以氧化石墨(GO)作为前驱体,在两种不同热剥离温度下制备了两类功能型单层石墨烯.其中第一类功能型单层石墨烯通过在较低温度及空气气氛下热剥离GO制备;第二类功能型单层石墨烯通过在氮气保护下高温热剥离GO得到;利用氮气吸附-脱附方法测定了两类样品的比表面积,利用电化学测试方法分析了其超电容性能.结果表明,通过低温热剥离的方式即可以有效剥离GO;两类样品均具有较高的BET比表面积.低温热剥离GO所制备的功能型单层石墨烯在2 mol/L KOH体系中的最大比电容值约为220 F/g;而通过高温热剥离GO所制备的功能型单层石墨烯虽然同样具有较高的BET比表面积,但其最大比电容值下降至约150 F/g.这表明通过低温热剥离GO所制备的功能型单层石墨烯具有更优异的超电容性能. Two kinds of functionalized graphene sheets were prepared via thermal exfoliation of graphite oxide(GO) precursor in two different routes.The first kind of functionalized graphene sheets was obtained by thermal exfoliation of GO at low temperature in air.The second kind was prepared by thermal exfoliation of GO at higher temperature in N2.The specific surface area of the two kinds of products was measured by using N2 adsorption-desorption analysis,while their supercapacitive behavior was evaluated by using electrochemical method.Results indicate that GO can be effectively thermally exfoliated even at relatively low temperature in air,and both kinds of products have high BET surface areas.Besides,the functionalized graphene sheets obtained via low temperature thermal exfoliation of GO have specific capacitance of about 220 F/g in aqueous KOH electrolyte;but those prepared via thermal exfoliation of GO at higher temperature in N2,with similar BET surface area,have lower specific capacitance of only about 150 F/g in the same electrolyte.This indicates that the first kind of functionalized graphene sheets has better supercapacitive behavior.
出处 《化学研究》 CAS 2010年第3期18-23,共6页 Chemical Research
基金 江苏省自然科学基金(BK2006195) 江苏省高校研究生科技创新计划(xm06-57)资助
关键词 功能型单层石墨烯 热剥离 制备 超电容性能 functionalized graphene sheets thermal exfoliation preparation supercapacitive behavior
  • 相关文献

参考文献16

  • 1Conway B E.Transition from "supercapacitor" to "battery" behavior in electrochemical energy storage[J].J Electrochem Soc,1991,138(6):1539-1548.
  • 2Fang Q L,Evans D A,Roberson S L,et al.Ruthenium oxide film electrodes prepared at low temperatures for electrochemical capacitors[J].J Electrochem Soc,2001,148(8):A833-A837.
  • 3Pang S,Anderson M A,Chapman T W.Novel electrode materials for thin-film ultracapacitors:Comparison of electrochemical properties of sol-gel-derived and electrodeposited manganese dioxide[J].J Electrochem Soc,2000,147(2):444-450.
  • 4Xu C,Bao S,Kong L,et al.Highly ordered MnO2 nanowire array thin films on Ti/Si substrate as an electrode for electrochemical capacitor[J].J Solid State Chem,2006,179(5):1351-1355.
  • 5Srinivasan V,Weidner J W.Studies on the capacitance of nickel oxide films:Effect of heating temperature and electrolyte concentration[J].J Electrochem Soc,2000,147(3):880-885.
  • 6Lin C,Ritter J A,Popov B N.Characterization of sol-gel derived cobalt oxide xerogels as electrochemical capacitor[J].J Electrochem Soc,1998,145(12):4097-4103.
  • 7Zheng M B,Cao J,Liao S T,et al.Preparation of mesoporous Co3O4 nanoparticles via solid-liquid route and effects of calcination temperature and textural parameters on their electrochemical capacitive behaviors[J].J Phys Chem C,2009,113:3887-3894.
  • 8Tanahashi I,Yoshida A,Nishino A.Electrochemical characterization of activated carbon-fiber cloth polarizable electrodes for electric double-layer capacitors[J].J Electrochem Soc,1990,137(10):3052-3057.
  • 9Fischer U,Saliger R,Bock V,et al.Carbon aerogels as electrode material in supercapacitors[J].J Porous Mat,1997,4(4):281-285.
  • 10马仁志,魏秉庆,徐才录,梁吉,吴德海.基于碳纳米管的超级电容器[J].中国科学(E辑),2000,30(2):112-116. 被引量:57

二级参考文献5

  • 1Niu C,Appl Phys Lett,1997年,70卷,11期,1480页
  • 2Sarangapani S,J Electrochem Soc,1996年,11卷,143期,3791页
  • 3Dai H,Science,1996年,272期,523页
  • 4Zheng J P,J Electrochem Soc,1995年,8卷,142期,2699页
  • 5Zheng J P,J Electrochem Soc,1995年,1卷,142期,L6页

共引文献56

同被引文献240

引证文献22

二级引证文献105

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部