45~#钢表面纳米晶层的高温磨损特性 被引量:6

The Sliding Wear Behavior of Nano-crystalline Surface Layer on 45~# Steel at Elevated Temperature
原文传递
导出
摘要 通过增压喷丸方式使45#钢实现表面纳米化,采用MMU-5G高温材料端面磨损试验机进行45#钢纳米晶层摩擦磨损性能随温度变化的试验,利用TEM表征喷丸后表层的组织,DSC与显微硬度研究纳米层的热稳定性,XPS和SEM表征磨损表面的成分及形貌.结果发现:当温度低于200℃时,喷丸样品表面硬度高,有效减少实际接触面积,耐磨性能优于未喷丸样品;在200~400℃之间时,纳米化样品表层组织结构中存在大量的晶界、位错、空位等缺陷为氧原子与金属原子提供更多的扩散通道,加速疏松的Fe2O3氧化物的形成与脱落,耐磨性能低于未喷丸样品;在400~550℃之间时,喷丸样品由于回复与再结晶,与未喷丸的耐磨性能基本一致. Nanocrystalline layers were fabricated on the surface of 45# steel by high pressure shot peening.Friction and wear tests of the nanocrystalline surface layer were implemented on a Model MMU-5G high temperature friction and wear tester.Microstructure of the surface layer was characterized by transmission electron microcopy(TEM).Differential scanning calorimetry(DSC)was employed to expatiate the thermal stability of the surface layer.Composition and morphology of the worn surfaces were also characterized by x-ray photoelectron spectroscopy(XPS)and scanning electron microscopy(SEM).Because the high hardness of the surface layer by the strengthening of fine grains and working hardening dramatically reduced the real area of contact,the wear resistance of shot peening sample was better than that of as-received sample at temperatures ranging from room temperature to 200 ℃.However,from 200 ℃ to 400 ℃ the as-received sample showed better tribological behavior that of the surface layer.It was because defects,e.g.grain boundary,dislocation,vacancy induced by the process of surface nanocrystallization were in favor of the diffusions of oxygen ions inwards and/or metal ions outwards,and hence accelerated the formation and breakdown of the loose oxide scale.Friction and wear of untreated and treated samples were comparable from 400 ℃ to 550 ℃ because of the recovery and growth of grain of the nanocrystalline layer.
出处 《摩擦学学报》 EI CAS CSCD 北大核心 2010年第3期285-290,共6页 Tribology
基金 广东省教育部产学研结合项目(2008B09050084) 粤港关键领域重点突破招标项目(TC09B863-2)的资助
关键词 45#钢 表面纳米化 喷丸 磨损 45#steel surface nanocrystallization shot peening wear
  • 相关文献

参考文献15

  • 1冯淦,石连捷,吕坚,卢柯.低碳钢超声喷丸表面纳米化的研究[J].金属学报,2000,36(3):300-301. 被引量:84
  • 2Liu G, Wang S C, Lou X F, et al. Low carbon steel with nano - structured surface layer induced by high - energy shot peening [J]. Script Mater, 2001,44 (8) : 1 791 -1 795.
  • 3吕晓仁,王胜刚,刘阳,李曙.纳米化纯铁在干摩擦及油润滑条件下的磨损行为研究[J].摩擦学学报,2007,27(1):20-24. 被引量:12
  • 4Wang Z B, Tao N R, Li S, et al. Effect of surface nanocrystallization on friction and wear properties in low carbon steel[ J ]. Materials Science and Engineering A, 2003, 352 : 144 - 149.
  • 5陈康敏,王树奇,杨子润,王峰,崔向红,潘励.钢的高温氧化磨损及氧化物膜的研究[J].摩擦学学报,2008,28(5):475-479. 被引量:37
  • 6李国宾,关德林,张明星.表面纳米化中碳钢在干摩擦条件下的摩擦磨损性能研究[J].摩擦学学报,2008,28(1):39-43. 被引量:14
  • 7Holmberg K, Ronkainen H, Laukkanen A, et al. Residual stresses in TiN, DLC and MoS2 coated surfaces with regard to their tribological fracture behaviour [ J ]. Wear, 2009, 267 : 2 142-2 156.
  • 8Nguyen T D, Kim Y J, Han J G, et al. Oxidation of TiZrAlN nanocomposite thin films in air at temperatures between 500 and 700℃ [J]. Thin Solid Films, 2009, 517:5 216 -5 218.
  • 9Mai Y J, Jie X H, Liu L L, et al. Thermal stability of nanocrystalline layers fabricated by surface nanocrystallization [J]. Appl Surf Sci, In Press, Corrected Proof.
  • 10Tu J P, Jie X H, Mao Z Y, et al. The effect of temperature on the unlubricated sliding wear of 5CrNiMo steel against 40 MnB steel in the range 400 -600°[ J]. Tribol Int, 1998, 31:347 - 353.

二级参考文献28

共引文献138

同被引文献71

引证文献6

二级引证文献31

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部