DZ468合金高周疲劳性能研究 被引量:11

STUDY ON HIGH CYCLE FATIGUE PROPERTIES OF DZ468 SUPERALLOY
原文传递
导出
摘要 本文研究了新型镍基高温合金DZ468的高周疲劳性能.结果表明:当应力比R=-1时,在900和760℃条件下,DZ468合金的疲劳强度分别为290和300 MPa.DZ468合金的高周疲劳试样断口由疲劳源、疲劳区和瞬断区组成.裂纹在表面、次表面和内部缺陷部位萌生,裂纹扩展具有第Ⅰ和第Ⅱ阶段,随应力幅增加裂纹扩展速率增大.光滑试样的疲劳裂纹扩展方式与变形机制间存在一定的关系,位错的平面滑移、交滑移和攀移的共同作用导致了合金在900和760℃时裂纹扩展具有两个阶段. The high cycle fatigue properties of a new type Ni-based superalloy DZ468 were investigated in this paper.The high cycle fatigue strengths of DZ468 alloy at 900 and 760℃with a ratio of stress R=-1 reach 290 and 300 MPa,respectively.The high cycle fatigue fractures of DZ468 alloy were composed of fatigue source,fatigue district and final stage.Cracks originate from surface, sub-surface and inner defect of sample.At 900 and 760℃,stageⅠand stageⅡcrack propagation could be observed from fatigue fracture,which was caused by the combination action of planar slip, cross slip and climb of dislocations.With increasing of stress value,the crack propagation rate quickly increase.A correlation exists between the crack propagation mode and deformation mode.
出处 《金属学报》 SCIE EI CAS CSCD 北大核心 2010年第6期708-714,共7页 Acta Metallurgica Sinica
关键词 镍基高温合金 高周疲劳性能 断口 Ni-based superalloy high cycle fatigue property fracture
  • 相关文献

参考文献22

  • 1于忠峰 郑志 刘恩泽 于永泗 朱耀宵.中国腐蚀与防护学报,2008,28:277-277.
  • 2宁礼奎,郑志,谭毅,刘恩泽,佟健,于永泗,王华.一种新型定向凝固镍基高温合金抗热腐蚀性能的研究[J].金属学报,2009,45(2):161-166. 被引量:16
  • 3刘恩泽 孙树臣 涂赣峰 郑志 宁礼奎 张凌峰.金属学报,2009,45:1217-1217.
  • 4Hoffelner W. Metall Trans, 1982; 13A: 1245.
  • 5Sajjadi S A, Nategh S. Mater Sci Eng, 2001; A307:158.
  • 6Liu Y, Yu J J, Xu Y. Mater Sci Eng, 2007; A454:357.
  • 7Hoffetner W, Gudmundson P. Eng Fract Mech, 1982; 16: 365.
  • 8Jones B F. Int J Fatigue, 1984; 6:75.
  • 9Pope D P, Ezz S S. Int Met Rev, 1984; 29:136.
  • 10Sieborger D, Knake H, Glatzel U. Mater Sci Eng, 2001; A298:26.

二级参考文献14

  • 1马书伟,郑运荣,于熙泓,阮中慈.Ni_7Hf_2/Ni_3Al共晶的微观组织特征[J].中国有色金属学报,1996,6(4):158-162. 被引量:2
  • 2师昌绪.中国高温合金四十年[M].北京:中国科学技术出版社,1996..
  • 3Shinata Y. Oxid Met, 1987; 27:315.
  • 4Zhu R Z, Guo M J, Zuo Y. Oxid Met, 1987; 27:253.
  • 5Santorelli R, Sivieri E, Reggiani R C. Mater Sci Eng, 1989; A120:283.
  • 6Yang J X, Zheng Q, Sun X F, Guan H R, Hu Z Q. Mater Sci Eng, 2007; A465:100.
  • 7Yeh A C, Sato A, Kobayashi T, Harada H. Mater Sci Eng, 2008; A490:445.
  • 8Zhu Y X. In: Antolovich S D, Stusrud R W, Mackay R A, Anton D L, Khan T, Kissinger R D, Klarstrom D L eds., Superalloys 1992, Pennsylvania: TMS, 1992:145.
  • 9Kearsey R M, Beddoes J C, Jones P, Au P. Interrnetallics, 2004; 12:903.
  • 10Kablov E N. Chemistry, 2005; 46:155.

共引文献66

同被引文献124

引证文献11

二级引证文献50

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部