废物水泥窑共处置产品中重金属释放模型研究——混凝土路面场景 被引量:9

Model of heavy metals releasing in cement produced from co-processing waste in cement kiln——ased on concrete pavement scenario
下载PDF
导出
摘要 通过模拟煅烧试验制取水泥熟料,并制得混凝土样品。在混凝土路面场景分析的基础上,参照欧盟固体中无机组分有效量测试方法(EA NEN7371),以pH=3.2的HNO3/H2SO4溶液(质量比为1∶2)为浸取液,在液固比为20 L/kg条件下,对混凝土样品进行模拟浸出实验;参照欧盟块状材料中无机组分的扩散实验方法(EA NEN7375)测定混凝土样品中重金属的有效释放量。模拟浸出实验结果表明,Cr、Ni和Cd在浸出过程中扩散控制是其释放的主要因素。在此基础上建立了重金属在混凝土路面中的释放模型。实验室实测累积释放量(实测值)与模型预测累积释放量(预测值)的拟合检验结果表明,实测值与预测值之间差异不显著,释放模型能较好地预测混凝土路面中重金属的长期累积释放量。 Cement clinker was prepared by simulating cement calcination, and the obtained clinker was used to produce concrete samples. On the basis of concrete pavement scenario analysis, the simulated leaching test of concrete samples which refers to EA NEN7371 was conducted to study the heavy metal releasing model. In the simulated leaching test, a blend of thick HNO3 and H2SO4 (weight ratio of 1 : 2, pH of 3.2) applied as extraction solvent and liquid to solid ratio was 20 to 1, the maximum release amount of heavy metals from concrete was determined according to EA NEN7375. Result showed that diffusion control was the major release mechanism of the Cr, Ni and Cd, and the leaching model of heavy metals in concrete pavement was built on that basis. The independent t-test of the predicted results and the measured ones showed that the no significant difference was found between the measured values and predictive values, they were fitting very well. The release model could forecast the cumulative release amount of heavy metals in concrete excellently.
出处 《环境污染与防治》 CAS CSCD 北大核心 2010年第7期5-9,43,共6页 Environmental Pollution & Control
基金 国家"十一五"科技支撑计划项目(No.2007BAC16B03)
关键词 水泥窑共处置 混凝土路面 重金属 释放 co-processing in cement kiln concrete pavement heavy metal release
  • 相关文献

参考文献19

  • 1乔龄山.水泥厂利用废弃物的有关问题(五)——水泥厂利用废弃物的基本准则[J].水泥,2003(5):1-9. 被引量:14
  • 2KOSSON D S,VAN DER SLOOT H A,SANCHEZ F,et al.An integrated framework for evaluating leaching in waste management and utilization of secondary materials[J].Environmental Engineering Science,2002,19(3).
  • 3PETER N D,LORNE A G.Scenario analysis in environmental impact assessment:improving explorations of the future[J].Environmental Impact Assessment Review,2007,27(3):206-219.
  • 4KOSSOR D S,VAN DER SLOOT H A,EIGHMY T T.An approach for estimation of contaminant release during utilization and disposal of municipal waste combustion residues[J].Journal of Hazardous Materials,1996,47(1/2/3).
  • 5VAN DER SLOOT H A.Comparison of the characteristic leaching behavior of cements using standard (EN 196-1) cement mortar and an assessment of their long-term environmental behavior in construction products during service life and recycling[J].Cement and Concrete Research,2000,30(7).
  • 6GARRABRANTS A C,SANCHEZ F,KOSSON D S.Changes in constituent equilibrium leaching and pore water characteristics of a Portland cement mortar as a result of carbonation[J].Waste Management,2004,24(1):19-36.
  • 7SANCHEZ F,GERVAISB C,GARRABRANTS A C,et al.Leaching of inorganic contaminants from cement-based waste materials as a result of carbonation during intermittent wetting[J].Waste Management,2002,22(2):249-260.
  • 8VAN DER SLOOT H A.Characterization of the leaching behaviour of concrete mortars and of cement stabilized wastes with different waste loading for long term environmental assessment[J].Waste Management,2002,22(2).
  • 9SERCLERAT I,MOSZKOWICZ P,POLLET B.Retention mechanisms in mortars of the trace metals contained in Portland cement clinkers[J].Waste Management,2000,20(2/3):259-264.
  • 10SANCHEZ F,GARRABRANTS A C,VANDECASTEELE C,et al.Environmental assessment of waste matrices contaminated with arsenic[J].Journal of Hazardous Materials,2003,96(2/3):229-257.

二级参考文献36

  • 1王文兴.中国酸雨成因研究[J].中国环境科学,1994,14(5):323-329. 被引量:212
  • 2朱雪梅,刘建国,黄启飞,王琪.固体废物水泥窑共处置技术应用及存在问题[J].中国水泥,2006(4):45-49. 被引量:46
  • 3赵娜娜,李丽,易爱华,罗程钟,黄启飞.POPs废物处置技术多目标决策筛选研究[J].环境科学研究,2007,20(3):164-167. 被引量:14
  • 4李洪珍.我国酸雨的区域化研究[A].见:朱钟杰.酸雨文集[C].北京:中国环境科学出版社,1989.208-216.
  • 5李文华 杨修.环境与发展[M].北京:科学技术文献出版社,1984.80-83.
  • 6Mokrzycki E, Uliasz-Boche Czyk A, Sarna M. Use of alternative fuels in the Polish cement industry [J]. Applied Energy, 2003,74 ( i ) : 101-111.
  • 7Trezza M A, Scian A N. Waste with chrome in Portland cement clinker production [ J]. J Hazard Materl, 2007,147(1/2) : 188-196.
  • 8Petkovic G, Engelsen C J, Breedveld G, et al. Environmental impact from the use of recycled materials in road construction: method for decision-maklng in Norway [ J ]. Resources, Conservation and Recycling, 2004,42 (3) : 249-264.
  • 9Aubert J E, Husson B, Sarramone N. Utilization of municipal solid waste incineration (MSWI) fly ash in blended cement Part 2. Mechanical strength of mortars and environmental impact [ J ]. J Hazard Matefi, 2007,146(1/2) : 12-19.
  • 10van der Sloot H A, Hoede D, Cresswell D J F, et al. Leaching hehaviour of synthetic aggregates [J]. Waste Manag, 2001,21 (3) : 221-228.

共引文献102

同被引文献129

引证文献9

二级引证文献39

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部