QT500-7井盖上表面缩凹形成机理及防治措施

Formation Mechanism and Prevention Methods of Depressions in the Top Surface of QT500-7 Manhole Covers
下载PDF
导出
摘要 球铁井盖用大平面朝上的浇注工艺,在其筋或筋与筋交汇处的上表面常会出现一些缩凹,严重影响井盖的质量,甚至造成较高的废品率。通过分析缩凹部位的微元体凝固过程及缩凹形成机理,比较了井盖结构改进前后热节圆直径的变化,结果认为:防止缩凹的关键是保证实现顺序凝固,保持浇注过程中补缩通道畅通。并从结构设计及铸造工艺设计两方面提出了防止球铁井盖上表面缩凹的措施,这些方法在生产实践中已得到检验。 Depressions in surface occurs on the surface of the junction of ribs when ductile cast iron manhole cover is produced by a casting process with large section upside,which results in a higher casting defective rate.The paper analyzes the solidification process of a differential element and the shrinkage mechanism and compares the variation of hot spot circle diameter before and after modification.The results show that directional solidification to maintain a smooth feeding is critical to avoid the shrinkage.Some prevention methods were proposed from two aspects of structural design and casting processing which has been verified by production practice.
作者 陈闹清 梁伟
出处 《山西科技》 2010年第4期112-114,共3页 Shanxi Science and Technology
基金 山西省科技攻关项目(项目编号:20090321071)
关键词 表面缩凹 补缩通道 热节圆 凝固特点 depression in surface feeding passage hot spot circle solidification characteristics
  • 相关文献

参考文献1

二级参考文献24

  • 1李嘉荣,柳百成.球墨铸铁件缩孔缩松的形成及其预测[J].现代铸铁,1993,13(1):32-40. 被引量:16
  • 2李嘉荣,柳百成,向华兵,童汉京,谢永通.湿型球墨铸铁件收缩特性的试验研究[J].现代铸铁,1995,15(3):3-9. 被引量:3
  • 3姚忻 丁少兰 吴学明 等.铸铁石墨形态的转变及生长动力学[J].金属学报,1986,22(4):358-360.
  • 4中国机械工程学会铸造分会.铸造手册(铸铁)第2版[M].北京:机械工业出版社,2002..
  • 5Karsay I, et al. Heavy ductile iron castings composition effect on graphite structure[J].AFS Trans, 1961, 69:672-679.
  • 6Stefanescu D M, Theory of solidification and graphite growth in ductile iron[A].ductile iron handbook[C]. US: AFS, 1992.
  • 7Wallace J F. Effects of minor elements on the structure of the ductile irons[J]. AFS Transactions, 1975, 83:363-378.
  • 8Kurz W, Fisher D J. Fundamentals of solidification [M].Aedermansdorf: Trans tech publications Ltd, 1989.
  • 9Stefanescu D M. Fundamentals of solidification of iron-based alloys and composites. Technical forum[A]. C1ATF 61st world foundry congress[C]. Beijing, 1995.
  • 10Motz J M, Wolters D B. Solidification of spheroderical graphite iron[J]. AFS Trans,1988(2):68-79.

共引文献20

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部