摘要
采用化学溶液法在SiC/Si上制备了YMnO3薄膜。XRD结果显示所制备的薄膜为六方YMnO3,且具有部分择优取向生长。拉曼光谱和XPS的结果验证了样品为六方纯相YMnO3。以Pt为顶电极,测试了YMnO3薄膜的电滞回线,结果显示YMnO3薄膜具有良好的铁电性质。
The YMnO3 thin film was prepared on SiC/Si by chemical solution deposition. The result of XRD displays that the sample is hexagonal phase with partly c-axis orientation. The Raman and XPS spectra indicate the sample is compose of pure hexagonal YMnO3. P-E hysteresis loop of hexagonal YMnO3 films deposited on SiC/Si was measured. It is seen that the films have good ferroelectric performance.