Semi-solid Al7Si0.3Mg alloy slurry, which is grain-refined by yttrium, is manufactured by low temperature pouring. The effects of grain-refined by yttrium on the morphology and the grain size of the primary α-Al in semi-solid Al7Si0.3Mg alloy are researched. The results indicate that semi-solid Al7Si0.3Mg alloy with particle-like and rosette-like primary α-Al can be prepared by low temperature pouring from liquid Al7Si0.3Mg alloy grain-refined by yttrium. The grain size and particle morphology of primary α-Al in Al7Si0.3Mg alloy are markedly improved by 0.5 wt pet Y. The refining mechanism of Y on the morphology and the grain size of the primary α-Al in semi-solid Al7Si0.3Mg alloy are delved.
Semi-solid Al7Si0.3Mg alloy slurry, which is grain-refined by yttrium, is manufactured by low temperature pouring. The effects of grain-refined by yttrium on the morphology and the grain size of the primary α-Al in semi-solid Al7Si0.3Mg alloy are researched. The results indicate that semi-solid Al7Si0.3Mg alloy with particle-like and rosette-like primary α-Al can be prepared by low temperature pouring from liquid Al7Si0.3Mg alloy grain-refined by yttrium. The grain size and particle morphology of primary α-Al in Al7Si0.3Mg alloy are markedly improved by 0.5 wt pet Y. The refining mechanism of Y on the morphology and the grain size of the primary α-Al in semi-solid Al7Si0.3Mg alloy are delved.
基金
supported by the Natural Science Foundation of Jiangxi Province(No.0650047)
the Science and Technology Program of the Education Departmentof Jiangxi Province (Nos.GJJ09229 and GJJ10470)