动态硫化EPDM/PP热塑性弹性体制备工艺研究 被引量:14

STUDY ON PREPARATION TECHNOLOGY OF DYNAMIC VULCANIZED EPDM/PP THERMOPLASTIC ELASTOMER
下载PDF
导出
摘要 研究了不同硫化体系 ,硫化时间 ,硫化剂的用量 ,共混温度 ,橡塑比 ,填充炭黑和软化剂的用量对动态硫化 EPDM/ PP共混物性能的影响。研究结果表明 :酚醛硫化体系制得的 EPDM/ PP共混物加工性能和力学性较佳 ,硫化时间在 10~ 15 min,硫化剂的用量以完全交联 EPDM为宜 ,共混温度控制在 170℃~ 190℃ ,橡塑比 70 / 3 0~ 5 0 / 5 0 ,填充炭黑在 40份以内 ,软化剂在 2 The effects of different curing systems,curing time,content of curing agents,blending temperature,ratio of rubber to plastics and content of filler carbon and oil on properties of dynamic vnlcanizated EPDM/PP blend were investigated.The results showed that a phenolic resin curing system provides the blends with excellent mechanical properties and processability,10~15min’s curing time and content of curing agents which crosslinked rubher fully were better.When blending temperature was 170℃~190℃,ratio of EPDM/PP was 70/30~50/50,content of filler carbon and oil was within 40phr,20phr,respectivly.blend had better properties.
出处 《胶体与聚合物》 1999年第1期24-27,共4页 Chinese Journal of Colloid & Polymer
关键词 动态硫化 聚丙烯 三元乙丙橡胶 热塑性弹性体 EPDM PP Dynamic vulcanization Preparation technology
  • 相关文献

参考文献4

二级参考文献6

共引文献42

同被引文献157

引证文献14

二级引证文献66

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部