高温过热蒸汽处理木材的吸湿解吸特性 被引量:15

Moisture Absorption and Desorption Characteristics of Superheated Steam-Treated Wood under High Temperature
下载PDF
导出
摘要 以日本柳杉为试材,经温度为140,160,180℃,相对湿度为0,60%,100%过热蒸汽处理后,考察并分析其在不同环境温度和相对湿度条件下的吸湿解吸特性和吸湿滞后现象。结果表明:高温过热蒸汽处理木材的水分吸着等温线的类型没有发生变化;吸湿、解吸过程中,在同一环境湿度下,高温高湿处理后木材的水分吸着量低于低温处理后木材的水分吸着量;水分吸着量随处理木材温度和相对湿度的增高呈减少趋势;处理前后的木材均有吸湿滞后现象;高温高湿处理后木材的吸湿滞后现象比低温条件处理木材的吸湿滞后现象明显。 Specimens from Japanese Sugi(Cryptomeria japonica)wood was treated with superheated steam under the temperature of 140,160,180 ℃ and the relative humidity(RH)of 0,60%,100% to investigate the moisture absorption and desorption characteristics and moisture absorption hysteresis phenomenon of treated wood under different environmental temperature and RH.The results showed that the type of the isotherm of the wood treated under high temperature superheated steam was not changed,that under the same environmental humidity,the amount of moisture sorption of the wood under high temperature and RH was lower than that of specimen under low temperature during moisture absorption and desorption process,that the amount of moisture sorption of the wood presented a trend of decreasing with the increasing temperature and RH,and that all specimens showed a hysteresis phenomenon of the moisture absorption,especially for the specimen under high temperature and RH.
出处 《林业科学》 EI CAS CSCD 北大核心 2010年第11期110-114,共5页 Scientia Silvae Sinicae
基金 国家自然科学基金资助项目(30871981)部分内容
关键词 高温过热蒸汽处理 木材 吸湿解吸特性 treated under high temperature superheated steam wood moisture absorption and desorption characteristics
  • 相关文献

参考文献13

  • 1程万里,刘一星,齐华春,師岡敏朗,則元 京.木材过热蒸汽干燥过程中的收缩应力(Ⅰ)——径向收缩应力特征[J].东北林业大学学报,2004,32(6):32-34. 被引量:13
  • 2程万里,刘一星,師岡敏朗,则元京.高温高压蒸汽干燥过程中木材的收缩应力特征[J].北京林业大学学报,2005,27(2):101-106. 被引量:16
  • 3程万里,刘一星,師岡敏朗.高温高压蒸汽条件下木材的拉伸应力松弛[J].北京林业大学学报,2007,29(4):84-89. 被引量:8
  • 4大島克仁.2002.遇熱水蒸気氖下での木材の力学特性.京都大学農学部修士論文.
  • 5東原貴志,師岡淳郎,則元京.2000.水蒸気処理木材の压缩变形固定とその機構.木材学会誌,46(4):291-297.
  • 6東原貴志,師岡淳郎,則元京.2001.熱処理木材の压缩变形固定とその機構.木材学会誌,47(3):205-211.
  • 7顾炼百.2004.木材加工工艺学.北京:中国林业出版社.
  • 8日本木材学会.1985.木材科学实验书1.物理·工学编.日本:东京中外产业调查会.
  • 9Cheng Wanli,Morooka T,Wu Qinglin,et al.2008.Transverse mechanical behavior of wood under high temperature and pressurized steam.Forest Products Journal,58(12):63-67.
  • 10Cheng Wanli,Morooka T,Liu Yixing,et al.2004.Shrinkage stress of wood during drying under superheated steam above 100℃.Holzforschuag,58(4):423-427.

二级参考文献31

  • 1程万里,刘一星,齐华春,師岡敏朗,則元 京.木材过热蒸汽干燥过程中的收缩应力(Ⅰ)——径向收缩应力特征[J].东北林业大学学报,2004,32(6):32-34. 被引量:13
  • 2程万里,刘一星,師岡敏朗,则元京.高温高压蒸汽干燥过程中木材的收缩应力特征[J].北京林业大学学报,2005,27(2):101-106. 被引量:16
  • 3DWIANTO W, MOROOKA T, NORIMOTO M. Method for measuring viscoelastic properties of wood under high temperature and high pressure steam conditions[J]. J Wood Sci, 1999, 45: 373-377.
  • 4DWIANTO W, MOROOKA T, NORIMOTO M. Stress relaxation of sugi wood ( Cryptomeria japonica D. Don) in radial compression under high temperature steam[J]. Holzforschung, 1999, 53 (5):541-546.
  • 5HIGASHIHARA T, MOROOKA T, NORIMOTO M. Permanent fixation of transversely compressed wood by steaming and its mechanism[J].Mokuzai Gakkashi,2000,46(4):291-297.
  • 6NORIMOTO M. Large compressive deformation in wood [ J ]. Mokuzai Gakkashi , 1993,39(8) :867-874.
  • 7INOUE M, NORIMOTO M, TANAHASHI M. Steam or heat fixation of compressed wood[J]. Wood and Fiber Sci,1993, 25 (3) 224-235.
  • 8SUMI H. High-temperature drying of wood Ⅲ: influence of temperature and heating-treatment time on types of static-bending failure of western hemlock [ J ]. Moku zai G akkashi, 1982,28 ( 8 ): 489-494.
  • 9KAWASAKI Y. The moisture distribution and dimensional change of Japanese cedar ( Cryptomeria Japonica D. Don) columns after high temperature drying[J]. Wood Industry, 1998,53(4): 166-171.
  • 10YOSHIDA T, HASHIZUMI T, FUJIMOTO N. High-temperature drying characteristics of boxed-heart square timber of Karamatsu and sugi: influences of high-temperature conditions with low humidity on drying properties[J]. Wood Industry, 2000,55(8) :357-362.

共引文献26

同被引文献221

引证文献15

二级引证文献73

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部