Preparation and Reaction Mechanism of Red Mud based Ceramic Simple Bricks 被引量:1

Preparation and Reaction Mechanism of Red Mud based Ceramic Simple Bricks
原文传递
导出
摘要 In order to utilize solid wastes,ceramic simple bricks with high performances were made from industrial solid wastes such as red mud,fly ash and poor clay shale as main raw materials in this paper.The phase compositions and microstructures were tested by XRD,SEM and EPMA.The experimental results show that the water absorption is 45.64%,the porosity is 58.91%,bulk density is 1.29 g·cm-3,compressive strength is 54.91 MPa,bending strength is 29.52 MPa,freeze-thaw resistance is 29.28 MPa,specific heat capacity at constant pressure is 1.31 J·g-1·K-1,thermal diffusivity is 5.89×10-3 cm2·s-1,and thermal conductivity is 1.15×10-2 W·cm-1·K-1.These effects of additives and preparation process to the properties and microstructures were discussed in detail.The reaction mechanism was also discussed.The results of the reaction mechanism show that there has wollastonite and feldspar generated during the process of firing while Ca gathered around the feldspar,and then Ca would displace K and generated cacoclasite. In order to utilize solid wastes,ceramic simple bricks with high performances were made from industrial solid wastes such as red mud,fly ash and poor clay shale as main raw materials in this paper.The phase compositions and microstructures were tested by XRD,SEM and EPMA.The experimental results show that the water absorption is 45.64%,the porosity is 58.91%,bulk density is 1.29 g·cm-3,compressive strength is 54.91 MPa,bending strength is 29.52 MPa,freeze-thaw resistance is 29.28 MPa,specific heat capacity at constant pressure is 1.31 J·g-1·K-1,thermal diffusivity is 5.89×10-3 cm2·s-1,and thermal conductivity is 1.15×10-2 W·cm-1·K-1.These effects of additives and preparation process to the properties and microstructures were discussed in detail.The reaction mechanism was also discussed.The results of the reaction mechanism show that there has wollastonite and feldspar generated during the process of firing while Ca gathered around the feldspar,and then Ca would displace K and generated cacoclasite.
作者 吴建锋
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2010年第6期1001-1005,共5页 武汉理工大学学报(材料科学英文版)
基金 Funded by the 11th Five-Year National Key Technology R&D Program(2008BAC41B00)
关键词 red mud ceramic simple bricks addictives properties and microstructures reaction mechanism red mud ceramic simple bricks addictives properties and microstructures reaction mechanism
  • 相关文献

参考文献1

共引文献10

同被引文献12

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部