熔盐法制备氧化镁粉体及其活性研究

Study on Preparation of MgO Ultrafine Powder by Molten Salt Method and Its Activity
下载PDF
导出
摘要 以MgCl2.6H2O、CaCO3和LiCl为原料,采用熔盐法制备了MgO粉体。通过热重-差示扫描热量计(TG-DSC)、X射线衍射仪(XRD)、场发射扫描电子显微镜(SEM)等手段对反应过程及产物进行了分析和表征,同时采用水解动力学分析法研究了煅烧温度和时间对氧化镁粉体活性的影响。TG-DSC分析表明,650℃时CaCO3可完全反应;XRD分析表明,450℃保温3 h热处理,产物中有MgO生成。650℃保温3 h热处理,产物经无水乙醇洗涤后,全部为MgO晶体;SEM分析表明,所制备的氧化镁形貌为颗粒状,形状不规整,大小介于50~250 nm之间;水解动力学分析法表明,当温度大于500℃、保温时间超过3 h后,随着热处理温度的升高和时间的延长,MgO粉体活性下降。 MgO powders were prepared through molten salt synthesis with MgCl2·6H2O, CaCO3 and LiCI. The reaction process and product were analyzed and characterized by using TG-DSC, XRD and TEM. The influences of the calcining temperature and time on the activity of MgO powders were also studied by hydrolysis kinetics. The TG-DSC results showed that: When the temperature reached the 650 ℃, the calcium carbonate decomposed completely. The XRD results showed that: we can obtain product of MgO. If the materials have been prepared at 450 ℃ for 3 h. If the materials have been prepared at 650 ~C for 3 h, and the product was washed in anhydrous alcohol, we completely obtained MgO Crystal The SEM results showed that: The product shape for the granular and irregularity shape, with the size of about 50-250 nm. The hydrolysis kinetics results also showed that: when the temperature was up to or higher than 500 ℃ and heat preservation time is up to or higher than 3 h, the activity of MgO would decrease with the increase of temperature and holding time.
出处 《广东化工》 CAS 2010年第12期206-207,共2页 Guangdong Chemical Industry
关键词 熔盐法 氧化镁粉体 制备 活性 molten salt synthesis MgO ultrafine powder preparation activity
  • 相关文献

参考文献8

  • 1Thoms H,Eppie M,Reller A.The thermal decomposition of magnesium alcoholates to magnesia(MgO):Studies by IR and thermal analysis[J].Solide State Ionics,1997,101-103:79.
  • 2Arendt R H.Liquid-phase sintering of magnetically isotropic and anise by the reaction of BaFe2O4 with Fe2O3[J].Solid State Chem,1973,8(4):339-347.
  • 3张冰,曹传宝,许亚杰,朱鹤荪.熔盐法合成莫来石晶须[J].无机化学学报,2005,21(2):277-280. 被引量:30
  • 4Hashimoto S,Zhang S W,Lee W E,et al.Synthesis of magnesium aluminate spinel platelets from α-alumina platelet and magnesium sulfate precursors[J].Am Ceram Soc,2003,86(11):1959-1961.
  • 5Kim J H,Myung S T,Sun Y K.Molten salt synthesis of LiNi0.5Mn1.5O4 spinel for 5V class cathode material of Li-ion secondary battery[J].Electrochemical Acta,2004,49(2):219-227.
  • 6Wang X,Gao L S,Zhou F,et al.Large-scale synthesis of α-LiFeO2 nanorods by low-temperature molten salt synthesis method[J].Crystal Growth,2004,265(1-2):220-223.
  • 7Mishra B,Olson D L.Molten salt applications in materials processing[J].Physics and Chemistry of Solids,2005,66(2):396-401.
  • 8袁锐.用菱镁矿粉矿制备高纯镁砂的研究[J].中国非金属矿工业导刊,2003(5):24-25. 被引量:8

二级参考文献20

  • 1王维邦.耐火材料工艺学[M].冶金工业出版社,1983..
  • 2王堂任.磁电选矿[M].北京:冶金工业出版社,1986..
  • 3Hashimoto S, Yamaguchi A. J. Eur. Ceram. Soc., 2000,20:397-406.
  • 4Kajiwara M. J. Mater. Sci., 1987,22:1223-1228.
  • 5YANG Yu(杨彧),JIA Dian—zeng(贾殿赠),GE Wei—Wei(葛炜炜),et a1.wuji Huaxue Xuebao(Chinese J.Inorg.Chem.),2004,20(8):881—888.
  • 6Zhang B, Cao C B, Xiang X, et al. Chem. Commun., 2004, 2452-2453.
  • 7Mazdiyasmi K S, Brown L M. J, Am. Ceram. Soc,, 1972,55:548-552.
  • 8Bartsch M, Saruhan B, Schmucker M, et al. J. Am. Ceram.Soc., 1999,82:1388-1392.
  • 9Barnawal R, Villar M P, Garcia R, et al. J. A m. Ceram. Soc.,2001,84:951-961.
  • 10Tummala R R. J. A m. Ceram. Soc., 1991,74:895-908.

共引文献35

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部