Surface modification of wollastonite particles using titanate as a modification agent incorporated by simultaneous wet ultra-fine grinding in a laboratory stirred mill was investigated.The physical,physic-chemical and application properties of the modified wollastonite were measured and evaluated.The results showed that grinding intensity markedly influences the modification effect because of the mechano chemical effect.The hydrophilic surface of wollastonite was turned into a hydrophobic one after modification.The interaction between titanate and wollastonite under wet grinding circumstances was studied.It was suggested that physical adsorption and chemical adsorption of titanate coexisted on the wollastonite surface.The mechanical properties of polyethylene（PE） filled with the modified wollastonite powder were markedly improved.
Surface modification of wollastonite particles using titanate as a modification agent incorporated by simultaneous wet ultra-fine grinding in a laboratory stirred mill was investigated.The physical,physic-chemical and application properties of the modified wollastonite were measured and evaluated.The results showed that grinding intensity markedly influences the modification effect because of the mechano chemical effect.The hydrophilic surface of wollastonite was turned into a hydrophobic one after modification.The interaction between titanate and wollastonite under wet grinding circumstances was studied.It was suggested that physical adsorption and chemical adsorption of titanate coexisted on the wollastonite surface.The mechanical properties of polyethylene（PE） filled with the modified wollastonite powder were markedly improved.
基金
supported by the National Key Technologies R & D Program of China(No.2008BAE60B06)