In order to develop a more economical pretreatment method for electroless nickel plating, a dielectric barrier discharge （DBD） plasma at atmospheric pressure was used to improve the hydrophilicity and adhesion of poly （ethylene terephthalate） （PET） nonwoven fabric. The properties of the PET nonwoven fabric including its liquid absorptive capacity （WA）, aging behavior, surface chemical composition, morphology of the surface, adhesion strength, surface electrical resistivity and electromagnetic interference （EMI）- shielding effectiveness （SE） were studied. The liquid absorptive capacity （WA） increased due to the incorporation of oxygen-containing and nitrogen-containing functional groups on the surface of PET nonwoven fabric after DBD airplasma treatment. The surface morphology of the nonwoven fibers became rougher after plasma treatment. Therefore, the surface was more prone to absorb tin sensitizer and palladium catalyst to form an active layer for the deposition of electroless nickel. SEM and X-ray diffraction （XRD） measurements indicated that a uniform coating of nickel was formed on the PET nonwoven fabric. The average EMI-SE of Ni-plating of PET nonwoven fabric maintained a relatively stable value （38.2 dB to 37.3 dB） in a frequency range of 50 MHz to 1500 MHz. It is concluded that DBD is feasible for pretreatment of nonwoven fabric for electroless nickel plating to prepare functional material with good EMI-SE properties.
In order to develop a more economical pretreatment method for electroless nickel plating, a dielectric barrier discharge （DBD） plasma at atmospheric pressure was used to improve the hydrophilicity and adhesion of poly （ethylene terephthalate） （PET） nonwoven fabric. The properties of the PET nonwoven fabric including its liquid absorptive capacity （WA）, aging behavior, surface chemical composition, morphology of the surface, adhesion strength, surface electrical resistivity and electromagnetic interference （EMI）- shielding effectiveness （SE） were studied. The liquid absorptive capacity （WA） increased due to the incorporation of oxygen-containing and nitrogen-containing functional groups on the surface of PET nonwoven fabric after DBD airplasma treatment. The surface morphology of the nonwoven fibers became rougher after plasma treatment. Therefore, the surface was more prone to absorb tin sensitizer and palladium catalyst to form an active layer for the deposition of electroless nickel. SEM and X-ray diffraction （XRD） measurements indicated that a uniform coating of nickel was formed on the PET nonwoven fabric. The average EMI-SE of Ni-plating of PET nonwoven fabric maintained a relatively stable value （38.2 dB to 37.3 dB） in a frequency range of 50 MHz to 1500 MHz. It is concluded that DBD is feasible for pretreatment of nonwoven fabric for electroless nickel plating to prepare functional material with good EMI-SE properties.
基金
supported by National Natural Science Foundation of China (No.50833003)