硅烷偶联剂KH550对正硅酸乙酯杂化涂层抗腐蚀性能的影响 被引量:6

Effect of a Silane Coupling Agent on Corrosion Performance of Tetraethoxysilane Hybrid Coating
原文传递
导出
摘要 利用电化学测试和扫描电镜(SEM)研究了硅烷偶联剂KH550对正硅酸乙酯(TEOS)杂化涂层的改性.结果表明:添加硅烷偶联剂能够明显提高TEOS杂化涂层的耐腐蚀性和降低涂层开裂倾向;经180℃热处理制备的KH550改性涂层性能最佳,在3.5%NaCl溶液中的腐蚀电流密度约为2.701×10^(-9)A/cm^2,较铝合金基体的4.208×10^(-5)A/cm^2低4个数量级,从而对铝合金基体具有良好的防护效果. The effect of a silane coupling agent(KH550) on corrosion performance of tetraethoxysilane (TEOS) hybrid coatings was investigated using electrochemical measurements and scanning electron microscopy(SEM).It follows that the addition of the silane coupling agent can obviously improve the corrosion resistance and the anti-cracking performance of the TEOS coatings.Whilst examinations on effect of heat treatment on coating preparation revealed that a heat treatment at 180℃might lead the coating an optimal corrosion resistance.Correspondingly,the corrosion current density of the coating in 3.5%NaCl solution is about 2.701×10^-9A/cm^2,a four orders of the magnitude less than that of plain aluminium alloy.This suggests that the hybrid coating can protect the aluminium alloy well.
出处 《腐蚀科学与防护技术》 CAS CSCD 北大核心 2011年第1期49-52,共4页 Corrosion Science and Protection Technology
关键词 硅烷偶联剂 溶胶-凝胶 耐腐蚀性 杂化涂层 silane coupling agent sol-gel process corrosion protection hybrid coating
  • 相关文献

参考文献7

二级参考文献41

共引文献136

同被引文献580

引证文献6

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部