摘要
The Eu（III） separation in supported dispersion liquid membrane （SDLM）, with polyvinylidene fluoride membrane （PVDF） as the support and dispersion solution containing HNO3 solution as the stripping solution and Di（2-ethylhexyl） phosphoric acid （D2EHPA） dis- solved in kerosene as the membrane solution, was studied. The effects ofpH value, initial concentration of Eu（III） and different ionic strengths in the feed phase, volume ratio of membrane solution and stripping solution, concentration of HNO3 solution, concentration of carrier, different stripping agents in the dispersion phase on the separation of Eu（III） were also investigated, respectively. As a result, the optimum separation conditions of Eu（III） were obtained as the concentration of HNO3 solution was 4.00 mol/L, concentration of D2EHPA was 0.160 mol/L, and volume ratio of membrane solution to stripping solution was 30：30 in the dispersion phase, and pH value was 5.00 in the feed phase. Ionic strength had no obvious effect on the separation of Eu（III）. Under the optimum conditions studied, when initial concentration of Eu（III） was 1.00× 10^-4 mol/L, the separation rate of Eu（III） was up to 94.2% during the separation period of 35 min. The kinetic equation was developed in terms of the law of mass diffusion and the theory of interface chemistry. The results were in good agreement with the literature data.
The Eu（III） separation in supported dispersion liquid membrane （SDLM）, with polyvinylidene fluoride membrane （PVDF） as the support and dispersion solution containing HNO3 solution as the stripping solution and Di（2-ethylhexyl） phosphoric acid （D2EHPA） dis- solved in kerosene as the membrane solution, was studied. The effects ofpH value, initial concentration of Eu（III） and different ionic strengths in the feed phase, volume ratio of membrane solution and stripping solution, concentration of HNO3 solution, concentration of carrier, different stripping agents in the dispersion phase on the separation of Eu（III） were also investigated, respectively. As a result, the optimum separation conditions of Eu（III） were obtained as the concentration of HNO3 solution was 4.00 mol/L, concentration of D2EHPA was 0.160 mol/L, and volume ratio of membrane solution to stripping solution was 30：30 in the dispersion phase, and pH value was 5.00 in the feed phase. Ionic strength had no obvious effect on the separation of Eu（III）. Under the optimum conditions studied, when initial concentration of Eu（III） was 1.00× 10^-4 mol/L, the separation rate of Eu（III） was up to 94.2% during the separation period of 35 min. The kinetic equation was developed in terms of the law of mass diffusion and the theory of interface chemistry. The results were in good agreement with the literature data.
基金
Project supported by the National Natural Science Foundation of China (90401009)
the Action Plan for the Development of Western China of the Chinese Academy of Sciences (KZCX2-XB2-13)
Research Fund for Excellent Doctoral Thesis of Xi'an University of Technology (602-210805)