活化元素对CuW材料热变形性能及组织的影响 被引量:2

Effect of Activation Element on the Microstructure and Performance of the Hot Deformed CuW Alloy
下载PDF
导出
摘要 研究了含不同微量活化元素的CuW材料经热变形和退火处理后性能的变化。采用扫描电镜分析了材料变形和退火后的组织变化,探讨了活化元素对CuW材料热变形的影响机理。结果表明,在700℃下进行预热后,加入活化元素的CuW材料的热变形性较好。在450℃退火后,含活化元素Cr、Ti的CuW材料变形后具有较高的电导率和硬度。对Cu/W界面的EPMA分析表明,活化元素的添加使Cu/W界面实现了冶金结合,增强了变形中界面的抵抗力,减小了压缩变形中的界面断裂现象。 The properties of CuW alloys with different activated elements were studiedafter thermal deformations and the anneal.The microstructure variations of deformedalloys after the anneal treatment were observed by SEM,and the effect of differentactivated elements on the hot mechanisms of CuW alloys were discussed.The results show that CuW alloys added activated elements exhibit good deformation after preheating at 700 ℃.After annealing at 450 ℃,CuW alloys with activation element Cr,Ti have higher hardness and electrical conductivity.The Cu/W interfaces were analysed by EPMA,and it show that the metallurgical Cu/W interface is obtained after adding activated elements,this higher interfacial bond strength can resist to the shear stress emerged in the deformation,and the phenomena interfacial fracture is decreased during the deformation process.
出处 《电工材料》 CAS 2010年第4期15-19,共5页 Electrical Engineering Materials
基金 国家自然科学基金重点项目(50834003) 国家自然科学基金(50871085) 科技部863计划(2009AA03Z522) 陕西省重点学科建设专项资金资助项目支持
关键词 CUW 活化元素 热变形 退火 CuW activation element thermal deformation annealing
  • 相关文献

参考文献10

二级参考文献18

共引文献73

同被引文献12

引证文献2

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部