在港口码头工程中,通常采用耐海水腐蚀的钢质结构。但这些钢质结构物在海水介质和海洋环境中仍然遭受着严重的腐蚀,导致材料的变质和破坏,构件物穿孔,而且会使结构设备丧失其全部或局部的技术功能,严重影响着设计使用寿命较长的港口码头的安全使用,直接或间接给国民经济带来巨大损失。文章主要分析了码头腐蚀的原因以及对策。
In the port terminal project, it usually uses steel structures that resistant seawater corrosion. However, these steel structures still suffer from severe corrosion in seawater and the marine enviromnent which lead to deterioration and destruction of materials and component object hole, and aslo will make it loss whole or part of its technical features of structures and equipment, have a serious impact on the safe use of the port with longer life, and directly or indirectly cause huge losses to the national economy. This paper analyzes the causes and countermeasures of terminal corrosion.