摘要
比较了Er:YAG激光辐射对不同类型牙本质粘结效果的影响。选用正常牙本质(ND)和龋病影响牙本质(CAD),经Er:YAG激光辐射后,分别以不同方式处理牙本质表面:质量分数为38%的磷酸酸蚀(磷酸组),低剂量Er:YAG激光辐射(激光组)和空白处理(对照组)。应用激光共聚焦扫描显微镜观察牙本质粘结界面超微结构。结果表明,Er:YAG激光辐射后,不同方式处理同种牙本质和相同方式处理不同牙本质后粘结层厚度均无差别(显著性水平p>0.05),粘结树脂突长度有差别(p<0.05),其中ND组大于CAD组,质量分数为38%的磷酸酸蚀组的最大,低剂量激光辐射组的居中,对照组的最小。所以Er:YAG激光辐射正常牙本质后,经质量分数为38%的磷酸酸蚀处理,牙本质粘结界面的渗透性最好,可形成理想的树脂突。
Bonding interface changes on different types of dentin after Er：YAG laser irradiation is evaluated.Normal dentin（ND） group and caries affected dentin（CAD） group samples are respectively irradiated with Er：YAG laser,and then etching with 38% phosphoric acid（phosphoric acid group）,low-dose Er：YAG laser radiation（laser group） and no treatment（control group）.The bonding interface changes are assessed via confocal laser scanning microscope（CLSM）.There is no significant difference in thickness（p〉0.05） within the same group with different etching methods or among different groups with the same etching,however,significant differences are existed in the length of resin tags（p〈0.05）.Maximum resin-tags are achieved in the phosphoric acid group,while control group minimum.Resin-tags in the bonding interface of ND are longer than that of CAD.The adhesive can infiltrate well into dentin bonding interface to achieve a quite ideal resin tags in the ND groups etching with 38% phosphoric acid.
出处
《中国激光》
EI
CAS
CSCD
北大核心
2011年第3期121-126,共6页
Chinese Journal of Lasers
基金
福建省重点科技项目(2009N0034)
福建省科技厅青年人才项目(2007F3032)
福建师范大学医学光电科学与技术教育部重点实验室开放课题(JYG1005)资助课题