氨基化多壁碳纳米管的制备及其在复合材料中的应用 被引量:10

Preparation of amine-modified multiwalled carbon nanotubes and their use in composites
下载PDF
导出
摘要 采用不同链长的乙二胺(EDA)、己二胺(HMDA)和癸二胺(DMDA)对多壁碳纳米管(MW CNTs)进行了修饰。利用红外光谱、拉曼光谱、透射电镜及X射线光电子能谱对二元胺修饰的MW CNTs的化学结构进行了表征。结果表明:二元胺可以有效地修饰MW CNTs。经胺化修饰后,MW CNTs-EDA、MW CNTs-HMDA、MW CNTs-DMDA表面的N元素含量可分别达到3.52%、4.18%和2.88%,表明在相同的氨化条件下,己二胺的接枝率最高。进一步采用紫外-可见吸收光谱及全能稳定性分析仪对不同链长的二元胺修饰的氨基化MW CNTs在有机溶剂中的分散性进行了半定量的表征。结果显示:氨基化修饰有效改善了碳纳米管在极性溶剂中的分散稳定性,其中己二胺修饰的MW CNTs在乙醇中的分散稳定性最好。将MW CNTs-HMDA引入到传统的炭纤维/环氧树脂复合材料体系中,复合材料的冲击性能及弯曲性能均有较大提高。 Multiwalled carbon nanotubes(MWCNTs) were modified by a graft reaction of diamines with different chain lengths,such as ethylenediamine(EDA),hexamethylene diamine(HMDA) and decamethylene diamine(DMDA).FTIR,Raman spectroscopy,XPS and TEM were used to characterize their chemical structure.XPS indicated that the molar content of N on the surface of MWCNTs-EDA,MWCNTs-HMDA and MWCNTs-DMDA reached 3.52%,4.18% and 2.88% respectively under the same reaction conditions.The dispersion of MWCNTs in organic solvents before and after the modification was measured semi-quantitatively using UV-Vis spectra and a Turbiscan analyzer.It was found that the amino-modified MWCNTs improved their dispersion in polar solvents and MWCNTs-HMDA had the best dispersion stability.MWCNTs-HMDA were introduced into a traditional carbon fiber reinforced epoxy system to prepare three phase composites which showed remarkably improved flexural and impact strengths.
出处 《新型炭材料》 SCIE EI CAS CSCD 北大核心 2011年第2期89-97,共9页 New Carbon Materials
基金 国家高技术研究发展计划(863计划)项目(2009AA03Z528)~~
关键词 碳纳米管 二元胺 化学修饰 分散稳定性 复合材料 Carbon nanotubes Diamine Chemical modification Dispersion stability Composites
  • 相关文献

参考文献4

二级参考文献36

  • 1王国建,董玥,邱军,刘琳.聚苯乙烯修饰碳纳米管表面的研究[J].高等学校化学学报,2006,27(6):1157-1161. 被引量:8
  • 2汪长春,舒昶,府寿宽.侧基上带有C_(60)基团的聚苯乙烯的合成[J].高等学校化学学报,1996,17(9):1477-1481. 被引量:7
  • 3SERVICE R F. Superstrong nanotubes show they are smart, too [J]. Science, 1998, 281: 940-942.
  • 4QIAN D, DICKEY C, ANDREWS R, et al. Mechanical property characterization of a polymeric nanocompositc reinforced by graphitic nanofibers with reactives [J]. Applied Physics Letters, 2000, 76: 2868-2870.
  • 5POPOV V N. Carbon nenotubes:properties and application [J]. Materials Science and Engineering, 2004, 43: 61-102.
  • 6YOSHIYUKI HATTORI, HIROFUMI KANOH, FUJIO OKINO, et al. Direct thermal fluorination of single wall carbon nanohorns [J]. Phvs Chem. B 2004. 108: 9614-9618.
  • 7I-CHUN LIU, HSUAN-MING HUANG, CHING-YU CHANG, et al. Preparing a styrenic polymer composite containing well-dispersed carbon nanotubes: anionic polymerization of a nanotube-bound p-methylstyrene [J].Macromolecules, 2004, 37(2): 283-287.
  • 8MERCEDES A, PEDRO A, PILAR C, et al. Sidewall functionalization of single-walled carbon nanotubes with nitrile imines electron transfer from the substituent to the carbon nanotube [J]. J Phys Chem B, 2004,108(34): 12691-12697.
  • 9BANERJEE S, WONG S S. Synthesis and characterization of carbon nanotube-nanocrystal heterostructures[Y]. Nano Lett, 2002, 2(2): 195-200.
  • 10KONG H, GAO C, YAN D Y. Functionalization of multiwalled carbon nanotubes by atom transfer radical polymerization and defunctionalization of the products [J]. Macromolecules, 2004, 37: 4022-4030.

共引文献71

同被引文献157

引证文献10

二级引证文献34

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部