摘要
Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·（1.95-x）GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 （x=0.02,0.05,0.08,0.11,0.14,0.17）in mole percent.Intense blue（476 nm）,green（524 and 546 nm）and red（658 nm）emissions which identified from the 1G 4 →3H 6 transition of Tm3＋and the（2H 11/2 ,4S 3/2 ）→4I 15/2 ,4F 9/2 →4I 15/2 transitions of Er3＋,respectively,were simultaneously observed under 980 nm excitation at room temperature.The results show that multicolor luminescence including white light can be adjustably tuned by changing doping concentrations of Er3＋ion or the excitation power.In addition,the energy transfer processes among Tm3＋,Er3＋and Yb3＋ions,and up-conversion mechanisms are discussed.
Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·（1.95-x）GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 （x=0.02,0.05,0.08,0.11,0.14,0.17）in mole percent.Intense blue（476 nm）,green（524 and 546 nm）and red（658 nm）emissions which identified from the 1G 4 →3H 6 transition of Tm3＋and the（2H 11/2 ,4S 3/2 ）→4I 15/2 ,4F 9/2 →4I 15/2 transitions of Er3＋,respectively,were simultaneously observed under 980 nm excitation at room temperature.The results show that multicolor luminescence including white light can be adjustably tuned by changing doping concentrations of Er3＋ion or the excitation power.In addition,the energy transfer processes among Tm3＋,Er3＋and Yb3＋ions,and up-conversion mechanisms are discussed.
基金
Funded by the National Natural Science Foundation of China (No. 50772045)
the Society Development Foundation of Yunnan Province (No. 2007E036M)