采用水热方法合成出一种新型的间硝基苯甲酸稀土配位聚合物[Nd2（C7H4O4N）7H2O]n,并通过元素分析、红外光谱、X射线单晶结构分析对该配位聚合物进行了表征.标题配位聚合物的晶体属于三斜晶系,P1空间群,晶胞参数a=0.984 8（2）nm,b=1.131 4（2）nm,c=1.366 3（3）nm,α=69.22（3）,°β=82.48（3）°,γ=82.21（3）°,V=1.404 5（5）nm3,Dc=1.806 g/cm3,Z=1.结构分析表明：标题化合物是由稀土金属Nd（Ⅲ）和间硝基苯甲酸组成的配位聚合物,此聚合物通过Ln—O—C—O—Ln形成无限一维链状结构,进一步又通过分子间氢键连接形成复杂的三维氢键网络结构.
A new coordination polymer [Nd2（C7H4O4N）7（H2O）4]n was synthesized hydrothermally.It was characteristic by elemental analysis,IR spectroscopy and single-crystal X-ray diffraction.The crystal belongs to triclinic system,space group P1.The cell parameters are as follows： a=0.984 8（2）nm,b=1.131 4（2）nm,c=1.366 3（3）nm,α = 69.22（3）°,β=82.48（3）°,γ=82.21（3）°,V=1.404 5（5）nm3,Dc= 1.806 g/cm3,Z=1.The structure of the complex reveals that the title complex is constructed by lanthanide Nd（Ⅲ） and m-nitrobenzoic acid ligand.The infinite 1D Ln—O—C—O—Ln polymeric chains are connected into a complicated 3D H-bonding framework through numerous intermolecular hydrogen bonds.
出处
《北华大学学报（自然科学版）》
CAS
2011年第3期289-292,共4页
Journal of Beihua University（Natural Science）
基金
国家自然科学基金项目(21071071)
吉林大学无机合成与制备化学国家重点实验室资助项目(2010-15)
关键词
钕配聚合物
间硝基苯甲酸
水热合成
晶体结构
Neodymium coordination polymer
m-Nitrobenzoic acid
hydrothermal synthesis
crystal structure