冶金提纯多晶硅用坩埚内壁氮化硅涂层的制备 被引量:7

Preparation of SiP_3N_4 Coating in the Inwall of Crucibles Used for Polycrystalline Silicon Purification in Metallurgical Process
下载PDF
导出
摘要 选用四种溶液与不同含量的氮化硅粉体混合得到不同的悬浊液,在石英坩埚内壁制备了氮化硅涂层,并将其用于冶金法提纯多晶硅;用扫描电镜、电子探针等分析了多晶硅铸锭与坩埚内壁的粘连面积、铸锭表面微裂纹形貌和反应层厚度,得到与最佳多晶硅铸锭脱模相对应的制备涂层的工艺参数,同时分析了熔炼过程中氮化硅涂层与硅熔体间的反应机制。结果表明:将含质量分数为8%聚乙烯吡咯烷酮的乙醇溶液和质量分数为60%氮化硅的悬浊液喷涂到坩埚内壁上,并经210℃×15min烧结后的氮化硅涂层不易分解,坩埚内壁保持完整,铸锭的脱模效果最好;随熔炼温度升高氮化硅涂层分解加剧,在涂层与硅铸锭的接触面处形成了由大颗粒氮化硅组成的连续层,减小了坩埚和涂层中杂质向硅铸锭内部扩散的可能性。 Various suspensions were made by four kinds of solutions mixing with different Si3N4 powders contents; the Si3N4 coatings, which used for polycrystalline silicon purification, were prepared in quartz crucibles inwall; the adhesive area between polycrystalline silicon ingots and crucible, microcrack morphology on the ingots surface and thickness of reaction layers were analyzed by SEM, EPMA, and so on. The process parameters prepared coating matching with best polycrystalline silicon knockout were got and the reaction mechanism between Si3N4 coating and melt silicon in melting process was analyzed. The results show that the coating was prepared by spraying the suspensions including the ethyalcohd solution containing 8wt% PVP, 60wt% SiC on crucibles inwall, and the coating sintered at 210 ℃ for 15 min was not decompounded, the crucible inwall was integrated, and the knockout effect of the ingot was best. The dissolution of SiaN4 coating aggravated with the increase of smelting temperature. The continuous layer, which reduced the possibility of impurity diffusing from crucible and coating to silicon ingot interior, was consisted of large Si3N4 particles on the interface of coating and silicon ingot.
出处 《机械工程材料》 CAS CSCD 北大核心 2011年第6期8-12,75,共6页 Materials For Mechanical Engineering
关键词 太阳能电池 多晶硅 氮化硅涂层 坩埚 solar cell polycrystalline silicon Si3N4 coating crucible
  • 相关文献

参考文献14

  • 1ARAFUNE K, OHISHI E, SAI H,et al. Directional .solidification of polycrystalline silicon ingots by successive relaxation of super- cooling method[J]. J Crystal Growth, 2007,308(1): 5-9.
  • 2ISTRATOV A A, BUONASSISI T, PICKETT M D, et al. Control of metal impurities in "dirty" multicrystalline silicon for solar cells[J]. Material Science and Engineering B, 2006, 134(2/3) : 282-286.
  • 3CHANEY R E, VARKER C J. The erosion of materials in molten silicon[J]. J Electrochem Soc, 1976,123 (6) : 846-852.
  • 4EL-KADDAH, PIWONKA N H, BERRY T S, et al. Induc- tion melting of metals without a crucible: US, 5014769[P]. 1991-05-14.
  • 5温宏权,毛协民,张军,傅恒志.太阳能级硅的电磁约束感应熔炼[J].太阳能学报,1996,17(4):344-347. 被引量:4
  • 6RAVISHANKAR P S. Liquid encapsulated bridgman (LEB) method for directional solidification of silicon using calcium chloride[J]. J Crystal Growth, 1989,94 (1) : 62-68.
  • 7PHILIP R C, ROBERT V J, TRENTON N J. Preparation of reactive materials in a molten non-reactive lined crucible: US, 2872299[P]. 1959-02-03.
  • 8CISZEK T F. The capillary action shaping technique and its application [C]//Crystals-Growth, Properties, and Applica- tions. Berlin: Springer-Verlag: 1981 : 110-146.
  • 9杜光庭,周卫,侯悦.氮化硅涂层坩埚..中国:CN87206316U[P].1987-12-30.
  • 10恩格勒·M,莱斯尼亚克·C,乌伊贝尔·K.含有氮化硅的耐久性硬质涂层..中国:CN1955228A[P].2007-05-02.

二级参考文献3

共引文献3

同被引文献86

  • 1张伟娜,谭毅,许富民.显微组织对冶金法制备多晶硅电阻率的影响[J].机械工程材料,2008,32(1):17-20. 被引量:8
  • 2刘国玺,赵昆渝,李智东,马秋花,葛伟萍.常压下制备氮化硅陶瓷材料的研究[J].机械工程材料,2004,28(11):22-24. 被引量:6
  • 3陈宏,穆柏春,郑黎明.氮化硅微粉制备技术[J].辽宁工学院学报,2006,26(3):191-195. 被引量:17
  • 4邓海,杨德仁,唐骏,席珍强,阙端麟.铸造多晶硅中杂质对少子寿命的影响[J].太阳能学报,2007,28(2):151-154. 被引量:24
  • 5Wang C M. Microstruetural homogeneity improvement in Si3 N4 by a powder coating method[J ].Jourrml of Materials Science, 1996,31:4709.
  • 6Lee S W, Chae H B, Park D S, et al. Thermal conductivity of unidirectionally oriented Si3 N4/Si3 N4 composites[ J]. Journal of Materials Science, 2000,35:4487.
  • 7Nicolieh J P,Lences Z,Dressler W, et al. Phase quantification of ct-SiaN4/-SiC mixtures by X-ray powder diffraction analysis[ J]. Journal of Materials Science,2000,35 : 1427-1432.
  • 8Liu Y S, Cheng L F, Zhang L T, et al. Fabrication and characterization of SiO2 (f)/Si3 N composites [ J 1. Journal of University of Science and Technology Beijing, 2007,14 ( 5 ) :454-459.
  • 9S. Dumitrica. D. Vizman. J. P. Garandet. Numerical studies on a type of mechanical stirring in directional solidification method of mulltic- rystalline silicon for photovoltaic applications [ J]. Journal of Crystal Growth. 2012,01.011.
  • 10L. J. Liu ,Satoshi Nakano, Koichi Kakimoto. Carbon concentration and particle precipitation during directional solidification of multicrystal- line silicon for solar cells[J]. Journal of Crystal Growth. 2011,310: 2192 -2197.

引证文献7

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部