纳米功能化石墨烯/室温硫化硅橡胶复合材料的制备与表征 被引量:30

Preparation and characterization of nano functionalized graphene/room temperature vulcanized silicone rubber composites
原文传递
导出
摘要 用KH-550对氧化石墨进行改性,再对其进行还原,获得功能化石墨烯(FG),未经干燥的FG经超声处理后可以稳定分散在质量比9∶1的丙酮/水混合液中;在高速搅拌和超声分散条件下,将FG分散液分散到室温硫化(RTV)硅橡胶中,固化后得到纳米FG(nano-FG)/RTV硅橡胶复合材料。采用FTIR、TEM、SEM、XRD和DSC分析了FG及复合材料的结构和形貌。结果表明:KH-550连接到石墨烯片层表面上,使其片层起皱、折叠,部分发生了剥离,层间距增大到3.46A°;FG经过超声处理后剥离成透明至半透明的片层;nano-FG/RTV硅橡胶复合材料的断面结构为褶皱结构,不同于纯硅橡胶,也未出现微观相分离;与硅橡胶相比,复合材料的Tg、Tm和结晶度均有所提高。复合材料的力学性能测试结果表明,nano-FG对RTV硅橡胶具有明显的补强效果,当nano-FG质量分数为0.5%时,nano-FG/RTV硅橡胶复合材料的拉伸强度比纯RTV硅橡胶提高了一倍多,达到了0.43 MPa;断裂伸长率也提高了52%,达到了265%。 Graphite oxide was modified by KH-550,the modified graphite oxide was reduced to form functionalized graphene(FG) dispersing consistently in the acetone/water(mass ratio is 9∶1) solution by ultrasonic treatment before drying.The FG dispersion was intensively mixed for a certain time by ultrasonic treatment to disperse the nano-FG in α,ω-dihydroxy polydimethylsiloxane matrix and obtained an uniform and stable nano-FG/room temperature vulcanized(RTV) silicone rubber composite after curing.FTIR,TEM,SEM,XRD,and DSC analysis show that KH-550 bonds to the surface of FG sheet to make its layers wrinkled,folding and partially exfoliated,and broaden its layer spacing to 3.46.FG exfoliates into transparent or semi-transparent layers after ultrasonic treatment.The uniform and wrinkled cross-section morphology of nano-FG/RTV silicone rubber composite,which is different from that of pure silicone rubber,shows that there is no micro-phase separation between the two parts.Compared with the pure silicone rubber,the Tg,Tm and crystallinity of all the nano-FG/RTV silicone rubber composites are improved.Mechanical property tests show that nano-FG reinforces silicone rubber a lot.The tensile strength and the elongation at break of composite with 0.5wt% nano-FG are 0.43MPa and 265%,respectively.The tensile strength more than doubles and the elongation at break increases 52% compared with that of pure silicone rubber.
出处 《复合材料学报》 EI CAS CSCD 北大核心 2011年第4期40-45,共6页 Acta Materiae Compositae Sinica
基金 国家自然科学基金(51072059)
关键词 氧化石墨 纳米功能化石墨烯 室温硫化硅橡胶 复合材料 补强 graphite oxide nano functionalized graphene room temperature vulcanized silicone rubber composites strengthen
  • 相关文献

参考文献14

  • 1Novoselov K S, Geim A K, Morozov S V, et al. Electric field effect in atomically thin carbon films [J]. Science, 2004, 306 (5296) : 666-669.
  • 2BokobzaL, Rahmani M. Carbon nanotubes: Exceptional reinforcing fillers for silicone rubbers [J]. Kautschuk Gummi Kunststoffe, 2009, 3(3): 112-117.
  • 3Yao Yuan, Liu Changhong, Fan Shoushan. Anisotropic conductance of the multiwall carbon nanotube array/silicone elastomer composite film [J]. Nanotechnology, 2006, 17 (17): 4374-4378.
  • 4Park S, Kim K J, Nam J D, et al. Mechanical, dielectric, and magnetic properties of the silicone elastomer with multi-walled carbon nanotubes as a nanofiller [J]. Polymer Engineering and Science, 2007, 47(9): 1396-1405.
  • 5Vast L, Mekhalif Z, Fonseca electrical characterization of a charged with multi-wall carbon A, et al. Preparation and silicone elastomer composite nanotubes functionalized with 7- octenyltrichlorosilane [J]. Composites Science and Technology, 2007, 67(5): 880-889.
  • 6Chua T P, Mariatti M, Azizan A, et al. Effects of surface- functionalized multi-walled carbon nanotubes on the properties of poly(dimethyl siloxane) nanocomposites [J]. Composites Science and Technology, 2010, 70(4) : 671-677.
  • 7刘丰,郑秋红,李小红,丁涛,张治军.可分散性纳米二氧化硅增强硅橡胶[J].复合材料学报,2006,23(6):57-63. 被引量:22
  • 8张琦,田明,吴友平,刘力,童玉清,胡伟康,张立群.纳米氢氧化镁/橡胶复合材料的分散特性及分散机理[J].复合材料学报,2003,20(4):88-95. 被引量:31
  • 9Watcharotone S, Dikin D A, Stankovich S, et al. Graphene- silica composite thin films as transparent conductors [J]. Nano Letters, 2007, 7(7): 1888-1892.
  • 10Chou Shulei, Wang Jiazhao, Choucair M, et al. Enhanced reversible lithium storage in a nanosize silicon/graphene composite [J]. Electrochemistry Communications, 2010, 12 (2) : 303-306.

二级参考文献17

  • 1何颖,李春忠,干路平,丛德滋,胡彦杰.纳米二氧化硅补强硅橡胶的结构及性能[J].华东理工大学学报(自然科学版),2005,31(4):456-459. 被引量:21
  • 2Cochrane H,Lin C S.The influence of fumed silica properties on the processing,curing and reinforcement properties of silicone rubber[J].Rubber Chemistry and Technology,1993,66(1):48-60.
  • 3Friedlander S K.Synthesis of nanoparticles and their agglomerates aerosol reactors[EB/OL].http://www.wtec.org/Loyloa/nano/us.review/.
  • 4Friedlander S K,Jang H D,Ryu K H.Elastic behavior of nanoparticle chain aggregates[J].App Phys Lett,1998,72:173-175.
  • 5Friedlander S K.Polymer-like behavior of inorganic nanoparticle chain aggregates[J].Journal of Nanoparticle Research,1999,1(1):9-15.
  • 6Cgawa K,Vogt T,Ullmann M.et al.Elastic properties of nanoparticle chain aggregates of titania,alumina and iron oxide generated by laser ablation[J].J Appl Phys,2000,87(1):63-73.
  • 7Payne A R,Whittaker R E.Low strain dynamic properties of filled rubber[J],Rubber Chem Technol,1994,44(3):440-478.
  • 8Wu G,Asais S,Sumita M.Estimation of flocculation structure in filled polymer composites by dynamic rheological measurements[J].Colloid Polym Sci,2000,287(3):220-228.
  • 9Kluppel M,Schuster R H,Gert H.Structure and properties of reinforcing fractal filler networks in elastomers[J].Rubber Chem Technol,1997,70(2):243-255.
  • 10Jun Z L,Yue D Y.Nano-isothermal crystallization kinetics of polyamide 1010/montmorillonite nanocomposite[J].Polymer Engineering and Science,2004,44(5):861-867.

共引文献50

同被引文献359

引证文献30

二级引证文献173

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部