低氟CaF_2-CaO-Al_2O_3-MgO-SiO_2系精炼渣的性能 被引量:16

Research on Properties of Low Fluorine CaF_2-CaO-Al_2O_3-MgO-SiO_2 Refining Slag
原文传递
导出
摘要 设计了精炼铜-铬合金用低氟CaF2-CaO-Al2O3-MgO-SiO2五元渣系,并研究了其粘度、密度、表面张力及熔化温度等性能.结果表明,该渣系的熔化温度在1336~1402℃之间;高温下该渣系的密度和表面张力均随温度升高而减小,且随CaF2含量和MgO含量增加逐渐降低;增加CaF2添加量可降低渣系粘度;CaF2含量较低时,MgO含量增加也可降低渣系粘度,CaF2含量较高时,渣粘度在MgO含量为6%时最小,MgO含量续增加到9%时粘度反而上升.该渣系粘度较低,表面张力较小,具有良好的精炼效果. Low fluorine CaF2-CaO-AlO3-MgO-SiO2 slag system was used as refining slag for preparation of Cu-Cr alloy. Its viscosity, density, surface tension and melting temperature were studied. The results indicated that the melting temperature of the slag was between 1336-1402℃. The density and surface tension of CaFE-CaO-A1203-MgO-SiO2 slag decreased with increasing of temperature, adding of CaF2 and MgO could decrease its density and surface tension. Its viscosity decreased with increasing of MgO and CaF2 content, and achieved the minimum value when MgO content was 6%, and increased when MgO content up to 9% with 10% and 15% CaF2 content. The slag had lower surface tension and better fluidity, so the refining efficiency with it was very good.
出处 《过程工程学报》 CAS CSCD 北大核心 2011年第4期695-700,共6页 The Chinese Journal of Process Engineering
基金 国家自然科学基金资助项目(编号:50704011,50644016,50874027) 国家重点基础研究发展规划基金资助项目(编号:2007CB613504) 留学回国基金资助项目(编号:20081201-9)
关键词 铜-铬合金 电渣重熔 熔渣 粘度 密度 表面张力 Cu-Cr alloy electroslag remelting slag viscosity density surface tension
  • 相关文献

参考文献7

二级参考文献32

共引文献64

同被引文献194

引证文献16

二级引证文献65

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部