粉末触媒合成高品级金刚石的工艺研究 被引量:6

Study on the synthesis technology for high grade diamond with powder catalyst
下载PDF
导出
摘要 本文提出了金刚石合成的二阶段升温升压工艺,讨论了各工艺参数(暂停时间、台阶功率、台阶压力)对粉末触媒高温高压合成优质金刚石单晶的影响,并对实验现象进行了分析,确立了高品级金刚石的合成工艺。实验结果表明:暂停时间长短影响成核的数量,暂停时间长金刚石产量低,暂停时间短金刚石产量高,但晶形较差;随着台阶功率的增加,金刚石的成核量和产量呈减少趋势;台阶压力的高低影响成核的多寡,台阶压力低,成核少,合成温度偏低,台阶压力高,成核多,金刚石晶形差。实践证实该工艺更有利于腔体的温度稳定。 A diamond synthesis technology of two-step pressure-rising and temperature-increasing was put forward in this paper.Influences of technology parameters,such as pause duration,power and pressure steps,upon diamond synthesis with powder catalyst at high pressure and high temperature(HPHT) were discussed,and the experiment phenomena were analyzed.Furthermore,the technology for high grade diamonds synthesis was established.The results showed that pause duration affected the quantity of diamond nucleus.Longer pause time led to lower diamond yield,while shorter pause time led to higher yield of diamond,but in poorer crystal shape.The diamond nucleus and yield were inclined to decrease with step power increasing.The diamond nucleus would also be affected by step pressure.The diamond nucleus was fewer at low pressure step and the resultant low synthesis temperature.Higher pressure step resulted in more diamond nucleus,but the diamond crystal morphology became poor.
出处 《金刚石与磨料磨具工程》 CAS 北大核心 2011年第4期23-28,共6页 Diamond & Abrasives Engineering
基金 郑州市科技攻关计划(NO.08SGYG25121-2)资助项目
关键词 两阶段升温升压 工艺参数 金刚石成核 two-step temperature-increasing and pressure-rising technology parameters diamond nucleus
  • 相关文献

参考文献6

二级参考文献31

  • 1Zhang H M, Jia X P, Ma H A and Guo W. CHIN. PHYS. LETT. 2008, 25 (2667).
  • 2Chiu M C, Hsieh W P, Ho W Y. Wang D Y and Shieu F S 2005 Thin Solid Films 476 258.
  • 3Jiang W, Yang B W, Lu W Y, Yao Y, Zhang S X and Kou Z L, 2005 Diamond Abrasives Engin. 4 50.
  • 4Hong S M, Jiang J C, Gou L and Zhong Y M. 2003 Mater. Sci. Lett. 22 257.
  • 5Sun C Q, Xie H and Zhang W. 2000 J. Phys. D: Appl. Phys. 33 2196.
  • 6贾晓鹏.金刚石合成的溶剂理论及当今行业热点问题的探讨[c].中国超硬材料研讨会南京会议论文集,2001:1-11.
  • 7Liu X B, Jia X P, Ma H A, Han W, Guo X K, Jia H S. HPHT CHIN. PHYS. LETT. 2009, 26 (038102).
  • 8贾晓鹏.金刚石合成的溶剂理论及当今行业热点问题的探讨[A]..中国超硬材料研讨会南京会议论文集[C].南京,2001.1-11.
  • 9Bovenkerk H P, Bundy F P, Hall H T, et al. Preparation of diamond[J]. Nature, 1959, 184: 1094.
  • 10Novirov N V, Shulzhenko A A. In: Saito S, Fukunaga O, Yoshikawa M, eds [J]. Science and Technology of New Diamond. Tokyo Japan,1990:217 - 221.

共引文献10

同被引文献29

引证文献6

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部