Ti-IF钢连续退火组织演变及微观织构研究 被引量:4

Study on Microstructure Evolution and Micro-Texture in Ti-IF Steel During Continuous Annealing
原文传递
导出
摘要 利用背散射电子衍射(EBSD)技术,研究了不同连续退火温度下Ti-IF钢微观取向的演变规律,并对不同退火温度下退火板的力学性能进行研究。研究发现当退火温度较低时(780℃)织构分布相对随机,随退火温度升高,ND∥<111>织构比例增加,在860℃退火时得到的r值最高,同时ND∥<111>织构比例最高,但当退火温度继续升高到900℃时,所有取向的晶粒均得到发展,使ND∥<111>织构比例和退火板的r值降低。 Micro-orientations evolution of cold-rolled Ti-IF steel annealed at different temperature was investigated by means of electron back scatter diffraction(EBSD) technique,and the mechanical properties of annealed sheets were studied.The results show that: textures are random distributed at low-temperature(780℃),with the temperature increasing,ND∥111 texture ratio increases,and the maximum r value and ND∥111 texture ratio at 860℃ are gotten,while the annealing temperature continues to rise to 900℃,all textures are developed,causing the reduce of ND∥111 texture ratio and r value
出处 《钢铁研究学报》 CAS CSCD 北大核心 2011年第9期33-36,共4页 Journal of Iron and Steel Research
基金 国家高技术研究发展计划资助项目(2009AA03Z518)
关键词 TI-IF钢 连续退火 性能 微观织构 EBSD Ti-IF steel continuous annealing property micro-texture EBSD
  • 相关文献

参考文献6

二级参考文献52

共引文献46

同被引文献30

引证文献4

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部