A combination of photochlorination ofp-xylene and succedent Friedel-Crafts alkylation polymerization was firstly used in the preparation of the hypercrosslinked adsorptive resin. The data of GC-MS and GC showed that a series of chlorizates were produced when p-xylene was photochlorinated. Hypercrosslinked resins could be synthesized by copolymerization, self-polymerization of chlorizates or post crosslinking reaction. The chemical structure and micromorphology of the porous resins were characterized by BET, FF-IR, SEM and elementary analysis （EA）. The results showed that the novel adsorptive resins possess high BET surface near to 1038 m^2/g and large pore volumes range from 0.5 to 1.2 cm^3/g.
A combination of photochlorination ofp-xylene and succedent Friedel-Crafts alkylation polymerization was firstly used in the preparation of the hypercrosslinked adsorptive resin. The data of GC-MS and GC showed that a series of chlorizates were produced when p-xylene was photochlorinated. Hypercrosslinked resins could be synthesized by copolymerization, self-polymerization of chlorizates or post crosslinking reaction. The chemical structure and micromorphology of the porous resins were characterized by BET, FF-IR, SEM and elementary analysis （EA）. The results showed that the novel adsorptive resins possess high BET surface near to 1038 m^2/g and large pore volumes range from 0.5 to 1.2 cm^3/g.
基金
support of the National Natural Science Foundation of China(Nos.20574063 and 21004055)