不同表面处理对Ceramage聚合瓷黏结强度的影响 被引量:3

Effect of different surface treatments on shear bond strength of Ceramage polymer-ceramics
下载PDF
导出
摘要 背景:长期以来修复材料与基牙的黏接技术一直是口腔修复学的研究热点,其中尤为引人关注的是黏结工件的表面处理工艺。目的:对比观察8种表面处理方法对Ceramage聚合瓷黏结强度的影响,筛选适合Ceramage聚合瓷的表面处理方法。方法:将Ceramage聚合瓷制成试件80个,随机分成8组,分别采用喷砂,酸蚀,偶联剂,喷砂+酸蚀,喷砂+偶联剂,酸蚀+偶联剂,喷砂+酸蚀+偶联剂处理聚合瓷表面并与树脂黏结剂黏结,对照组不进行任何处理。在37℃水浴24h后测试样本剪切强度,并用扫描电镜观察处理后的聚合瓷表面形貌。结果与结论:各组的剪切强度值由高到低分别为:喷砂+酸蚀+偶联剂处理组(31.12±2.81)MPa,喷砂+酸蚀组(27.62±1.70)MPa,酸蚀+偶联剂组(27.31±2.18)MPa,喷砂+偶联剂组(26.91±1.97)MPa,喷砂组(24.23±2.03)MPa,偶联剂组(23.50±2.19)MPa,酸蚀组(17.61±2.14)MPa,对照组(8.13±0.63)MPa,除喷砂组、偶联剂组之间,喷砂+酸蚀组、喷砂+偶联剂组、酸蚀+偶联剂组之间比较差异无显著性意义外(P>0.05),其余组间比较差异均有显著性意义(P<0.05)。结果显示7种表面处理方法都提高了黏结强度,喷砂、酸蚀联合硅烷偶联剂处理的聚合瓷黏结强度最高,是适合Ceramage聚合瓷黏结的表面处理方法。 BACKGROUND:Repair materials and abutment bonding technology have always been the research focus of prosthodontics,particularly surface treatment process. OBJECTIVE:To observe the effect of six different surface treatments on Ceramage polymer-ceramic bond strength and to find the proper surface treatment method. METHODS:Eighty polymer-ceramic specimens were randomly divided into 8 groups,respectively,using the following 8 ways:A:No treatment;B:Sandblasting;C:Etching;D:Silane coupling agent;E:Sandblasting + etching;F:Blasting + silane coupling agent;G:Etching + silane coupling agent;H:Sandblasting + etching + silane coupling agent bonded with Panavia-F resin cement. After storage at 37 ℃ water for 24 hours,the specimens were subjected to a shear bond strength test. Surface morphology of polymer-ceramic was observed using scanning electron microscopy. RESULTS AND CONCLUSION:Shear strength values of 8 experimental group(MPa) from the highest to the lowest were as follows:H group(31.12±2.81) ,E group(27.62±1.70) ,G group(27.31±2.18) ,F group(26.91±1.97) ,B group(24.23±2.03) ,D group(23.50±2.19) ,C group(17.61±2.14) ,A group(8.13±0.63) . There was no significant difference between B and D groups as well as among E,F and G groups(P 0.05);the remaining groups were statistically significant between groups(P 0.05) . Seven kinds of surface treatment methods have increased the bond strength;Sandblasting group and Coupling group was significant higher than Etching groups;Sandblasting,etching in combination with silane coupling agent group showed the highest bond strength,which was the most proper surface treatment method for Ceramage polymer-ceramic bonding.
出处 《中国组织工程研究与临床康复》 CAS CSCD 北大核心 2011年第34期6331-6334,共4页 Journal of Clinical Rehabilitative Tissue Engineering Research
  • 相关文献

参考文献14

  • 1El Zohairy AA,De Gee AJ,Mohsen MM,et al.Microtensile bond strength testing of luting cements to prefabricated CAD/CAM ceramic and composite blocks.Dent Mater.2003;19(7):575-583.
  • 2于绍冰,郭天文,尹路.刷洗对两种聚合瓷表面形态、光泽和色彩影响的对比研究[J].口腔颌面修复学杂志,2008,9(2):102-105. 被引量:12
  • 3杨晶,罗云.影响瓷贴面与釉质粘结强度的研究进展[J].口腔颌面修复学杂志,2008,9(2):152-154. 被引量:5
  • 4Della Bona A,van Noort R.Shear vs.tensile bond strength of resin composite bonded to ceramic.J Dent Res.1995;74(9):1591-1596.
  • 5刘振海,张振庭,高卫民,郑东翔,温颖.表面处理对粘结剂与氧化锆粘结强度的影响[J].口腔颌面修复学杂志,2007,8(4):284-286. 被引量:9
  • 6Kussano CM,Bonfante G,Batista JG,et al.Evaluation of shear bond strength of composite to porcelain according to surface treatment.Braz Dent J.2003;14(2):132-135.
  • 7李婷,章浙锋,周谧,王航.喷砂表面处理技术在口腔全瓷修复中的应用[J].国际口腔医学杂志,2010,37(2):206-209. 被引量:10
  • 8Kern M,Thompson VP.Sandblasting and silica coating of a glass-infiltrated alumina ceramic:volume loss,morphology,and changes in the surface composition.J Prosthet Dent.1994;71(5):453-461.
  • 9Della Bona A,Donassollo TA,Demarco FF,et al.Characterization and surface treatment effects on topography of a glass-infiltrated alumina/zirconia-reinforced ceramic.Dent Mater.2007;23(6):769-775.
  • 10Addison O,Fleming GJ.The influence of cement lute,thermocycling and surface preparation on the strength of a porcelain laminate veneering material.Dent Mater.2004;20(3):286-292.

二级参考文献101

  • 1罗娟,王新知,刘学恒.纳米增韧牙科复合树脂的研究[J].临床口腔医学杂志,2007,23(7):394-396. 被引量:18
  • 2Alkhiary YM,Morgano SM,Giordano RA.Effects of acid hydrolysis and mechanical polishing on surface residual stresses of low-fusing dental ceramics[J].J Prosthet Dent,2003,90(2):133-142.
  • 3Burke FJ,Fleming G J,Nathanson D,et al.Are adhesive technologies needed to support ceramics? An assessment of the current evidence[J].J Adhes Dent,2002,4(1):7-22.
  • 4Blatz MB,Sadan A,Martin J,et al.In vitvo evaluation of shear bond strengths of resin to donsely-sintered highpurity zirconium-oxide ceramic after long-term storage and thermal cycling[J].J Prosthnt Dent,2004,91 (4):356-362.
  • 5Komine F,Tomic M,Gerds T,et al.Influence of different adhesive resin cements on the fracture strength of aluminum oxide ceramic posterior crowns[J].J Prosthet Dent,2004,92 (4):359-364.
  • 6Saygili G,Sahmali S.Effect of ceramic surface treatment on the shear bond strengths of two resin luting agents to all-ceramic materials[J].J Oral Rehabil,2003,30 (7):758-764.
  • 7Chang JC,Hart DA,Estey AW,et al Tensile bond strengths of five luting agents to two CAD-CAM restorative materials and enamel[J].J Prosthet Dent,2003,90 (1):18-23.
  • 8Della Bona A,Anusavice KJ,Shen C.Microtensile strength of composite bonded to hot-pressed ceramics[J].J Adhes Dent,2000,2(4):305-313.
  • 9Bottino MA,Valandro LF,Scotti R,et al.Effect of surface treatments on the resin bond to zirconium-based ceramic[J].Int J Prosthodont,2005,18(1):60-65.
  • 10Ozcan M,Vallittu PK.Effect of surface conditioning methods on the bond strength of luting cement to ceramics[J].Dent Mater,2003,19(8):725-731.

共引文献59

同被引文献30

  • 1魏士刚.金属烤瓷全冠修复后常见问题的分析及应对措施[J].中国社区医师(医学专业),2010,12(23):100-100. 被引量:2
  • 2洪岩松,李晶,艾红军,付斌.聚合瓷嵌体修复后牙牙体缺损效果分析[J].中国实用口腔科杂志,2009,2(6):359-360. 被引量:14
  • 3杜珍,汲平.纤维桩的分类及性能特点[J].口腔颌面修复学杂志,2007,8(3):227-228. 被引量:31
  • 4洪岩松,李晶,艾红军.后牙Ceramage聚合瓷嵌体的临床应用[J].中国医科大学学报,2007,36(4):447-448. 被引量:9
  • 5Shinya A,Yokoyama D, Lassila LV, et al. Three-dimen- sional finite element analysis of metal and FRC adhesive fixed dental prostheses[J]. Adhes Dent, 2008, 10(5): 365- 371.
  • 6Yokoyama D, Shinya A, Lassila LV, et ah Framework de- sign of an anterior fiber-reinforced hybrid composite fixed partial denture: a 3D finite element study [J]. International Journalof Prosthodontics, 2009, 22(4): 405-412.
  • 7Rappelli G, Putignano A. Tooth splinting with fiber-rein- forced composite materials: achieving predictable aesthetics [J]. Pract Proced Aesthet Dent, 2002, 14(6).. 495-500.
  • 8Van Heumen CC, van Dijken JW, Tanner J, et al. Five-year survival of 3-unit fiber-reinforced coinposite fixed partial dentures in the anterior area[J]. Dental Materials, 2009, 25 (6): 820-827.
  • 9Annett Dorner-Reisel,Christian Schurer,Eberhard Muller,et al.The wear resistance of diamond-like carbon coated and uncoated Co28Cr6Mo knee prostheses[J].Diamond and Related Materials,2004,13(4-8):823-827.
  • 10张磊,曹琦.不同树脂嵌体材料边缘微渗漏的对比研究[J].中国美容医学,2012,18(47):6960-6966.

引证文献3

二级引证文献12

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部