采用电化学方法制备了硫酸(H2SO4)和磺基水杨酸酸(SSA)共掺杂的导电聚乙烯醇/聚苯胺(PVA/PANI)复合膜,采用正交设计法优化工艺条件,研究了沉积银电流密度和时间、拉伸对复合膜电导的影响。采用红外光谱、X射线衍射、扫描电镜对复合膜进行表征。结果表明,最佳条件下获得的PVA/PANI复合膜电导率为22.72S/cm;在此复合膜上以50mA/cm2沉积2min银可使复合膜的电导显著提高到1250S/cm;对2种复合膜进行适当的拉伸可使其电导率分别提高20.74%和18.04%。复合膜有一定程度的结晶,经拉伸后其结晶度有所提高。
Conductive polyaniline （PANI） films co-doped with sulfosalicylic acid （SSA） and sulfuric acid （H2SO4） were prepared via electrochemical method on a poly （vinyl alcohol） （PVA） supporting film, and the optimum condition of preparation was found through an orthogonal design. The influences of deposited current density and time of silver （Ag） and stretching on the conductivity of composite films were also studied. The composite films were characterized by IR, XRD and SEM. The result showed that the conductivity of PVA/PANI composite film obtained under optimum conditions was 22. 72 S/cm. Deposited Ag by current density of 50 mA/cm2 for 2 min into prior film sequentially, the conductivity increased to 1250 S/cm significantly. Applying appropriate stretching to PVA/PANI and PVA/PANI/Ag composite films, the conductivity could be enhanced by 20. 74 % and 18. 04 % respectively, and the crystallinity was improved.
出处
《中国塑料》
CAS
CSCD
北大核心
2011年第10期38-43,共6页
China Plastics
关键词
聚乙烯醇
聚苯胺
银
电化学聚合
复合膜
电导率
拉伸
poly（vinyl alcohol）
polyaniline
silver
electrochemical synthesis
composite film
electric conductivity
stretching