口腔正畸用镍钛弓丝的腐蚀性及防腐蚀 被引量:4

Corrosion and anticorrosion of nickel-titanium arch wires in orthodontics
下载PDF
导出
摘要 背景:口腔正畸用镍钛弓丝临床使用后期常发生弓丝力学性能降低现象,严重影响了临床治疗效果,有研究表明口腔唾液电解质环境腐蚀是影响其性能的主要因素之一。目的:综述近年国内外关于口腔正畸用镍钛弓丝腐蚀性研究的进展。方法:采用计算机检索中国知网数据库CNKI 1995-01/2010-10,PubMed数据库和Elsevier(ScienceDirect)数据库1975-01/2010-10与正畸用镍钛弓丝腐蚀性相关得研究。结果与结论:在复杂的口腔环境中,温度、负载、氟离子等因素均能加速对正畸用镍钛弓丝的腐蚀,不同程度地影响正畸用镍钛弓丝的性能,降低正畸镍钛弓丝的机械性能,增大表面粗糙度进而延长了正畸治疗疗程,增加了正畸治疗成本。正畸用镍钛弓丝腐蚀所释放的镍离子降低了其生物安全性。防腐蚀处理能提高镍钛弓丝的抗腐蚀能力,主要应用表面处理技术,但目前安全有效的方法并不多,对正畸用镍钛弓丝的腐蚀和防腐蚀还有待于进一步深入研究。 BACKGROUND:Orthodontics with nickel-titanium arch wires often occurs the decrease of mechanical property after clinical application,and seriously affects the effect of clinical therapy.Studies show that corrosion in oral electrolyte is one of the most reasons.OBJECTIVE:To review the research progress on nickel-titanium arch wires in orthodontics recently at home and abroad.METHODS:Literatures related to corrosion of nickel-titanium arch wires in orthodontics from CNKI database,PubMed database and Elsevier(ScienceDirect) database were retrieved.RESULTS AND CONCLUSION:In complex oral environment,temperature,load,fluorinion and other factors can accelerate the corrosion of nickel-titanium arch wires,the property of nickel-titanium arch wires in orthodontics was influenced to some extent,and which reduced the mechanical properties of nickel-titanium arch wires in orthodontics,increased the roughness of surface and then prolonged the course of treatment,and increased the cost of orthodontic treatment.The release of nickel ion of nickel-titanium arch wires in orthodontics reduced its biological safety.Anticorrosion treatment can improve the corrosion resistance of nickel-titanium arch wires;surface treatment technology is mainly applied.However,safe and effective method is seldom at present,the corrosion and anticorrosion on nickel-titanium arch wires in orthodontics is needed to be further deeply studied.
出处 《中国组织工程研究与临床康复》 CAS CSCD 北大核心 2011年第38期7185-7188,共4页 Journal of Clinical Rehabilitative Tissue Engineering Research
基金 教育部科研基本费小额探索项目(lzujbky-2011-134) 中国科学院兰州化学物理研究所固体润滑国家重点实验室开放项目(0808) 兰州大学青年交叉学科创新基金(20091286) 兰州大学口腔医学科研扶持基金项目(2010-03)~~
  • 相关文献

参考文献35

  • 1Bourauel C,Fries T,Drescher D,et al.Surface roughness of orthodontic wires via atomic force microscopy,laser specular reflectance,and profilometry.Eur J Orthod.1998;20(1):79-92.
  • 2Shim HM,Oh KT,Woo JY,et al.Corrosion resistance of titanium silver alloys in an artificial saliva containing fluoride ions.J Biomed Mater Res B Appl Biomater.2005;73(2):252-259.
  • 3Siargos B,Bradley TG,Darabara M,et al.Galvanic corrosion of metal injection molded (MIM) and conventional brackets with nickel-titanium and copper-nickel-titanium arch wires.Angle Orthodontist.2007;77(2):355-360.
  • 4Iijima M,Endo K,Yuasa T,et al.Galvanic corrosion behavior of orthodontic archwire alloys coupled to bracket alloys.Angle Orthodontist.2006;76(4):705-711.
  • 5Hunt NP,Cunningham SJ,Golden CG,et al.An investigation into the effects of polishing on surface hardness and corrosion of orthodontic archwires.Angle Orthodo.1999;69(5):433-440.
  • 6Rondelli G,Vicentini B.Localized corrosion behaviour in simulated human body fluids of commercial Ni-Ti orthodontic wires.Biomaterials.1999;20(8):785-792.
  • 7Huang HH.Variation in surface topography of different NiTi orthodontic archwires in various commercial fluoride-containing environments.Dent Mater.2007;23(1):24-33.
  • 8Eliades T,Athanasiou AE.In vivo aging of orthodontic alloys:implications for corrosion potential,nickel release,and biocompatibility.Angle Orthodontist.2002;72(3):222-237.
  • 9陈志清.口腔材料学[M].2版.北京:人民卫生出版社,2001:153-154.
  • 10Liu IH,Lee TM,Chang CY,et al.Effect of load deflection on corrosion behavior of NiTi wire.J Dental Res.2007;86(6):539-543.

二级参考文献14

  • 1Sekiguchi y. Applications of shape memory alloys: Medical applications. In : Funakubo H, editor. Shape memory alloys [ M ]. New York : Gordon and Breach Science Publishers, 1987 ; 226 - 269.
  • 2Uo M, Watari F, Yokoyama A, Matsuno H, Kawasaki T. Dissolution of nickel and tissure response observed by X-ray scanning analytical microscopy [J]. Biomaterials, 1999,20(7) :747 - 755.
  • 3Grill A. Diamond-like carbon coatings as biocompatible materials-an overview [ J ]. Diamond and related materials, 2003, 12 ( 1 ) :166- 170.
  • 4Peltonen L. Nickel sensitity in general population contact dermatitis[J]. Biomaterials 1979,5( 1 ) :27 - 32.
  • 5Thomsen P, Ericson LE. Inflammatory cell response to bone implant surfacs, in The Bone Biomaterial Interface [ C ]. J E Davies ( ed ),University of Toronto Press,Toronto, 1991 ; 135 - 164.
  • 6Fergouson A B. The ionization of metal implants in living tissues[J]. J Bone Joint Surg(Am), 1960,42( 1 ) :77 - 9o.
  • 7Jones MI, McColl R, Grant DM, Parker KG, Parker TL. Protein adsorption and platelet attachment and activation, on TiN, TiC, and DLC coatings on titanium for cardiovascular applications [ J ]. J Biomed Mater Res,2000,52(4) :413 - 421.
  • 8Kapanen A, Ryhanen J, Danilov A, Tuukkanen J. Effect of nickeltitanium shape momory metal alloy on bone formation [ J ].Biomaterials, 2001,22 ( 11 ) : 2475 - 2480.
  • 9Wever D J, Veldhuizen AG, de Vries J, Busscher H J, Uggs DRA, van Horn JR. Electrochemical and surface characterization of a nickeltitanium alloy[J]. Biomaterials, 1998,19(7) :761 - 769.
  • 10Wataha JC, Lockwood PE, Marek M, Ghazi M, Ability of Nicontaining biomedical alloys to activate monocytes and endothelial cells in vitro[J] .J biomed Mater Res,1999(2) ,45:251 - 257.

共引文献17

同被引文献38

  • 1罗小安,林珊.正畸不锈钢弓丝的腐蚀与防腐蚀[J].口腔材料器械杂志,2007,16(3):147-149. 被引量:3
  • 2Lee H, Rho J, Messersmith PB. Facile conjugation of biomolecules onto surfaces via mussel adhesive protein inspired coatings[ J]. Adv Mater, 2009, 21(4) : 431 -434.
  • 3Neoh KG, Hu X, Zheng D, et al. Balancing osteoblast functions and bacterial adhesion on functionalized titanimn surfaces[J]. Biomaterials, 2012, 33 ( 10 ) : 2813 - 2822.
  • 4Bai YJ, Wang YB, Cheng Y, et al. Comparative study on the corro- sion behavior of Ti-Nb and TMA alloys for dental application in various artificial solutions[ J]. Mater Sci Engin C, 2011, 31 ( 3 ) : 702 - 711.
  • 5Qiu KJ, Lin W J, Zhou FY, et al. Ti-Ga binary alloys developed as potential dental materials[ J]. Mater Sci Engin C, 2014, 34 ( 1 ) : 474 - 483.
  • 6Jiang J, Zhu L, Zhu L, et al. Surface characteristics of a self-poly- merized dopamine coating deposited on hydrophobic polymer films [J]. Langmuir, 2011, 27(23) : 14180 - 14187.
  • 7Wang M, Yi D, Ping Z, et al. In vitro culture and directed osteo- genie differentiation of human pluripotent stem cells on pcptides- decorated two-dimensional microenvironment[J]. ACS Appl Mater Interfaces, 2015, 7(8): 4560-4572.
  • 8Qiu KJ, Liu Y, Zhou FY, et al. Microstructure, mechanical pro- perties, castability and in vitro biocompatibility of Ti-Bi alloys developed for dental applications[J]. Acta Biomater, 2015, 15 :254 -265.
  • 9Ahmed RA, Fadl-Allah SA, E1-Bagoury N, et al. Improvement of corrosion resistance and antibacterial effect of NiTi orthopedic mate- rials by chitosan and gold nanoparticles[ J]. Appl Surf Sci, 2014, 292 ( 3 ) : 390 - 399.
  • 10Hu X, Neoh K G, Shi Z, et al. An in vitro assessment of titanium functionalized with polysaccharides conjugated with vascular endothelial growth factor for enhanced osseointegration and inhibition of bacterial adhesion [ J ]. Biomaterials, 2010, 31 (34) : 8854 - 8863.

引证文献4

二级引证文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部