The influence of Ce on the solidification microstructures of M2 high speed steel was studied. The results show that Ce has the effect of alleviating the segregation of alloying elements such as W and Mo in high speed steel. With the addition of Ce, the amount of eutectic carbides is decreased and the flakes of the carbides are refined. Ce mainly segregates onto the interface between the eutectic carbide and austenite, and a Dart of Ce enters M2C carbide. Ce can also enhance the breaking and spheroidizing of the network eutectic carbides during high temperature heat treatment.
The influence of Ce on the solidification microstructures of M2 high speed steel was studied. The results show that Ce has the effect of alleviating the segregation of alloying elements such as W and Mo in high speed steel. With the addition of Ce, the amount of eutectic carbides is decreased and the flakes of the carbides are refined. Ce mainly segregates onto the interface between the eutectic carbide and austenite, and a Dart of Ce enters M2C carbide. Ce can also enhance the breaking and spheroidizing of the network eutectic carbides during high temperature heat treatment.
基金
ProjectsupportedbytheNationalNaturalScienceFoundationofChina( 5 93 710 3 4 )andthePostDoctoralScienceFoundation