摘要
The microstructures and free-volume evolutions of as-cast and pre-annealed Zr65Al7.5Ni10Cu12.5Ag5 bulk metallic glasses during rolling deformation have been investigated. No phase transformation is detected in the as-cast/rolled specimen. However,the structural stability of the glass against plastic deformation is worse after pre-annealing,indicated by nanocrystallization in preannealed/rolled specimens with large deformation degrees. Moreover,with increasing deformation degree,the free-volume content in a pre-annealed/rolled specimen increases at a lower average rate than that in an as-cast/rolled specimen.
The microstructures and free-volume evolutions of as-cast and pre-annealed Zr65Al7.5Ni10Cu12.5Ag5 bulk metallic glasses during rolling deformation have been investigated. No phase transformation is detected in the as-cast/rolled specimen. However,the structural stability of the glass against plastic deformation is worse after pre-annealing,indicated by nanocrystallization in preannealed/rolled specimens with large deformation degrees. Moreover,with increasing deformation degree,the free-volume content in a pre-annealed/rolled specimen increases at a lower average rate than that in an as-cast/rolled specimen.
基金
supported by the National Natural Science Foundation of China (50771064 and 50831003)