转炉冶炼新型耐候钢06CuPNi1Cr2

Smelting of a new-type weathering steel 06CuPNi1Cr2 by converter
原文传递
导出
摘要 为高效利用资源,充分利用低镍铬红土矿中的镍铬元素,研发了一种新型耐候钢06CuPNi1Cr2.针对转炉冶炼耐候钢过程金属液中铬元素氧化的问题,研究并讨论了冶炼温度和一氧化碳分压对脱碳保铬的影响.转炉冶炼06CuPNi1Cr2耐候钢模拟实验表明,顶吹氧气强度为3.0~3.3 m3.min-1.t-1,终点碳的质量分数为0.02%~0.05%,冶炼终点温度控制在1680~1 700℃时,脱碳保铬效果显著. A new-type weathering steel 06CuPNi1Cr2 was developed by high-efficiently utilizing nickel and chromium in low nickel-chromium laterite ores.The influences of bath temperature and the partial pressure of carbon monoxide on decarburization and keeping chromium were studied and discussed to solve the problem of chromium oxidation in steelmaking.06CuPNi1Cr2 smelting experiments show that the effects of decarburization and keeping chromium are remarkable when the oxygen top-blowing is 3.0 to 3.3m3·min-1·t-1,the mass fraction of final carbon is 0.02% to 0.05% and the end-point smelting temperature is 1680 to 1700℃.
出处 《北京科技大学学报》 EI CAS CSCD 北大核心 2011年第12期1453-1457,共5页 Journal of University of Science and Technology Beijing
基金 教育部新世纪优秀人才支持计划资助项目(NCET07-0067) 中央高校基本科研业务费专项(FRF-BR-09-020B)
关键词 炼钢 耐候钢 转炉 红土矿 脱碳 steelmaking weathering steel converters laterite nickel chromium decarburization
  • 相关文献

参考文献7

二级参考文献37

共引文献184

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部