3种树脂水门汀对CAD/CAM全瓷-牙本质剪切强度的比较 被引量:5

Evaluation of bond strength of three resin cements on CAD/CAM ceramic-dentin
原文传递
导出
摘要 目的:评价3种树脂水门汀对CAD/CAM全瓷-牙本质剪切强度的影响。方法:选取新鲜拔除的人磨牙30颗,制备牙本质黏结面,随机分为3组(n=10),分别选用全酸蚀树脂水门汀RelyX ARC、自酸蚀树脂水门汀Clearfil DCBond和自黏结树脂水门汀RelyX Unicem对CAD/CAM硅酸锂玻璃全瓷进行黏结,测试3种树脂水门汀对CAD/CAM全瓷-牙本质的剪切强度,并通过立体显微镜观察牙本质的黏结界面。采用SPSS11.0软件包对数据进行统计学分析。结果:RelyX ARC组的剪切强度为(15.90±6.15)MPa,Clearfil DC Bond组的剪切强度为(14.41±5.07)MPa,而RelyXUnicem组的剪切强度为(23.29±7.39)MPa,与前2组相比有显著性差异(P<0.05)。立体显微镜观察显示,3组黏结断面均位于牙本质与树脂水门汀之间。结论:自酸蚀树脂水门汀及自黏结树脂水门汀与CAD/CAM硅酸锂玻璃陶瓷修复体的黏结强度不低于传统全酸蚀树脂水门汀,且临床操作简便,为临床全瓷黏结提供了更多便利与选择。 PURPOSE: To evaluate the bond strength of 3 resin cements on ceramic-dentin.METHODS: Thirty sound human posterior tooth were selected for this study and the flat dentin surfaces were prepared.The specimens were divided into 3 groups(n=10) randomly,which were bonded to the CAD/CAM ceramics with RelyX ARC(etch-and-rinse adhesive),Clearfil DC Bond(self-etching resin cement) and RelyX Unicem(self-adhesive resin cement).The bond strengths were tested and the bond surfaces were observed under stereoscopic microscope.SPSS 11.0 software package was used for statistical analysis.RESULTS: The shear bond strength of RelyX ARC and Clearfil DC Bond was(15.90±6.15)MPa and(14.41±5.07)MPa,respectively.The shear strength of RelyX Unicem was(23.29±7.39)MPa,significantly higher than the others.The shear strength between the three resin cements was significantly different(P〈0.05).CONCLUSION: Clearfil DC Bond and RelyX Unicem can achieve a successful bond on CAD/CAM ceramic crowns.
出处 《上海口腔医学》 CAS CSCD 北大核心 2012年第1期20-23,共4页 Shanghai Journal of Stomatology
基金 上海市卫生局资助项目(2009074)~~
关键词 树脂水门汀 剪切强度 牙本质 全瓷 Resin cement Shear bond strength Dentin All-ceramic
  • 相关文献

参考文献15

  • 1Richard D. Stutes.椅旁CAD/CAN牙科修复系统的历史与临床应用现状(英文)[J].上海口腔医学,2006,15(5):449-455. 被引量:27
  • 2Thompson JY,Rapp MM,Parker AJ.Microscopic and energydipersive X-ray analysis of surface adaptation of dental cements todental ceramic surfaces[J].J Prosthet Dent,1998,79(4):378-383.
  • 3Yiu-Fai M,Lai SN,Cheung GP,et al.Micro-tensile bond testingof resin cements to dentin and an indirect resin composite[J].Dent Mater,2002,18(8):609-621.
  • 4Scalone BA,Mutlu O,Felipe VL,et al.Microtensile bondstrength of a resin cement to felspathic ceramic after differentetching and silanization regimens in dry and aged conditions[J].Dent Mater,2007,23(11):1323-1331.
  • 5谭晓蕾,张少锋,郭航,郭煜.硅烷偶联剂及自酸蚀粘结剂对VitaMark Ⅱ与牙本质粘结强度的影响[J].口腔颌面修复学杂志,2009,10(2):109-112. 被引量:15
  • 6De Munck J,Vargas Marcos,Van Landuyt K,et al.Bonding ofan auto-adhesive luting material to enamel and dentin[J].DentMater,2004,20(10):963-971.
  • 7Viotti RG,Kasaz A,Pena CE,et al.Microtensile bond strength ofnew self-adhesive luting agents and conventional multistepsystems[J].J Prosthet Dent,2009,102(5):306-312.
  • 8Gladys S,Van Meerbeek B,Braem M,et al.Comparativephysico-mechanical characterization of new hybrid restorativematerials with conventional glass-ionomer and resin compositerestorative materials[J].J Dent Res,1997,76(4):883-894.
  • 9Gerth HU,Dammaschke T,Züchner Z,et al.Chemical analysisand bonding reaction of RelyX Unicem and Bifix composites-Acomparative study[J].Dent Mater,2006,22(10):934-941.
  • 10Hikita K,Van Meerbeek B,De Munck J,et al.Bondingeffectiveness of adhesive luting agents to enamel and dentin[J].Dent Mater,2007,23(1):71-80.

二级参考文献20

  • 1Saracoglu A, Cura C, Cotert HS. Effect of various surface treatment methods on the bond strength of the heat-pressed ceramic samples[J]. J Oral Rehabil, 2004, 31(8): 790-797
  • 2Kern M, Thomspon VP. Sandblasting and silica coating of glass-infiltrated alumina ceramic: Volumeloss, morphology, and changes in surface composition[J]. J Prosthet Dent, 1994, 71(5): 453-461
  • 3Chen JH, Matsumura H, AtsutaM. Effect of etchant, etching period, and silane priming on bond strength to porcelain of composite resin [J]. Oper Dent, 1998, 23(5): 250-257
  • 4Kwok hung, Yen chang Hwang. Bonding strength of porcelain repair system with various surfaee treatment. J Prosthet Dent, 1997, 78(3): 267-273
  • 5Brentel AS, Ozcan M, Valandro LF, et al. Microtensile bond strength of a resin cement to feldpathic ceramic after different etching and silanization regimens in dry and aged conditions[J].Dental Materials, 2007, 23(11): 1323-1331
  • 6Foxton RM, Nakajima M, Hiraishi N, et al. Relationship between ceramic primer and ceramic surface PH on the bonding of dual-cure resin cement to ceramic[J]. Dental Materials, 2003, 19(8): 779-789
  • 7Peumans M, Van Meerbeek B, Yoshiba Y. Porcelain veneers bonded to tooth structure: an ultra-morphological FESEM examination of the adhesive interface [J] . Dent Mater, 1999, 15(2): 105-119
  • 8DeMuncka J, V argasb M, Van Landuyt k, et al. Bonding of an auto-adhesive luting material to enamel and dentin[J]. DentMater, 2004, 20(10): 963-971
  • 9Lackey A.Shorten the learning curve:CEREC 3D brings ease of use to chairside CAD/CAM[J].Contemp Esthet and Rest Prac,2003,7(9 Suppl):4-6.
  • 10Schmidt B,Simon J.New CAD/CAM system combines simplicity with sophistication[J].Contemp Esthet and Rest Pract,2003,7(9Suppl):15-22.

共引文献40

同被引文献62

  • 1陈溯,张振庭.计算机辅助设计与计算机辅助制作后牙修复体的三年临床观察及失败病例分析[J].中华口腔医学杂志,2007,42(6):337-339. 被引量:6
  • 2王晓波,陈晖,张玉芹,等.前牙缺失金属烤瓷冠桥修复临床观察[J].中国美容医学,2012,21(z1):12.
  • 3于世凤.口腔组织病理学[M].北京:人民卫生出版社,2012:72-78.
  • 4何玉林.CEREC瓷嵌体的临床评价[J].实用口腔医学杂志,1997,13(3):783-784. 被引量:2
  • 5Kurbad A. The optical conditioning of Cerec preparations with scan spray[J]. Int J Comput Dent, 2000, 3 (4) : 269-279.
  • 6Federlin M, Manner T, Hiller KA, et al. Three-year clinical perfor- mance of cast gold vs ceramic partial crowns [J].Clin Oral Investig, 2007,11 (4) : 345-352.
  • 7Fasbinder DJ, Dennison JB,Heys D,et al. A elinical evaluation of chairside lithium disilicate CAD/CAM erowns:A two-year report [J]. J Am Dent Assoc, 2010, 141 (Suppl 2) : 10S-14S.
  • 8el-Mowafy OM1, Rubo MH, el-Badrawy WA. Hardening of new resin cements cured through a ceramic inlay [J]. Oper Dent, 1999, 24 (1): 38-44.
  • 9Sjogren G, Molin M, van Dijken JW. A 10-year prospective evalua- tion of CAD / CAM-manufactured (Ceree) ceramic inlays cemented with a chemically cured or dual-cured resincomposite [J]. Int J Prosthodont, 2004, 17 (2) ; 241-246.
  • 10DozicA1, Kleverlaan CJ, Meegdes M, et al. The influence of porcelain layer thickness on the final shade of ceramic restorations [J]. J Pros- thet Dent, 2003, 90 (6) : 563-570.

引证文献5

二级引证文献53

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部